分别采用埋弧焊、药芯焊丝 CO 2气体保护焊和焊条电弧焊工艺对 DH36耐蚀船板钢进行对接焊，然后在模拟油船货油舱下底板的腐蚀环境中进行腐蚀试验，研究了焊接工艺对焊缝金属组织和耐蚀性能的影响。结果表明：在3种焊接工艺下，焊缝金属的组织均主要由先共析铁素体、侧板条铁素体和针状铁素体组成；与焊条电弧焊和气体保护焊相比，采用埋弧焊得到的焊缝金属的耐蚀性能最优，这源于埋弧焊较高的热输入导致针状体素体数量减少；在三种焊接工艺下，焊缝金属中夹杂物的尺寸、分布均相似，它们对焊缝金属耐蚀性能的影响基本相同。
Corrosion resistant ship plate steels DH36 were welded by using submerged-arc welding,flux cored wire CO 2 gas shielded welding and shielded metal arc welding processes,and then corrosion experiments were carried out in the simulated environment around bottom plates of cargo oil tanks,the effects of welding processes on microstructure and corrosion resistance of weld metals were studied.The results show that under three welding processes,microstructure of the weld metals consisted predominantly of acicular ferrite,ferrite side-plate and proeutectoid ferrite.Compared with shielded metal arc welding and gas shielded welding,the weld metal prepared by submerged-arc welding had the best corrosion resistance,this due to the decrease of proeutectoid ferrite caused by higher heat input.Under three welding processes,the size and distribution of inclusion in weld metal were similar,and there was no obvious difference in the effects of inclusion on corrosion property of weld metal.
参考文献
| [1] | 孔小东;杨明波;童康明;朱梅五.焊接工艺对低合金海洋用钢焊接接头耐蚀性的影响[J].兵器材料科学与工程,2007(5):9-13. |
| [2] | 李继红;杨亮;张兴璇;张敏.超低碳微合金管线钢焊接接头的组织与冲击性能[J].机械工程材料,2014(6):75-78. |
| [3] | 宋洁;王哲;曹睿;张晓波;彭云;杜挽生;田志凌;陈剑虹.低碳贝氏体高强钢焊接接头的组织与拉伸性能[J].机械工程材料,2013(4):87-92. |
| [4] | 黄安国;王永生;李志远;张国栋.针状铁素体焊缝金属腐蚀行为的研究[J].材料保护,2004(3):6-8. |
| [5] | 黄桂桥.Cr对钢耐海水腐蚀性的影响[J].腐蚀科学与防护技术,2000(02):86-89. |
| [6] | 黄安国;李志远;余圣甫;周龙早;张国栋.低合金钢焊缝金属的腐蚀行为[J].焊接学报,2005(11):30-34. |
| [7] | 齐彦昌;彭云;田志凌;冯向阳.Ni对油船货油舱下底板焊缝耐蚀性的影响[J].材料热处理学报,2013(4):69-73. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%