利用无水硫酸铝和硫酸钠熔盐对多孔碳化硅陶瓷进行了表面改性处理,研究了熔盐反应后的物相组成和显微结构,并测试了改性前后多孔碳化硅陶瓷对烟气中 PM2．5的过滤性能.结果表明：在900℃下,硫酸铝、硫酸钠熔盐与碳化硅反应生成针状莫来石晶须,长度达到十几个微米,直径几百个纳米；熔盐改性多孔碳化硅陶瓷将柴油烟气中PM2．5质量浓度由大于280μg?m－3降低到小于150μg?m－3,过滤效果优于未改性多孔碳化硅陶瓷的(200μg?m－3)；莫来石晶须可以阻挡烟气中颗粒物的运动,使其沉积在晶须间,提高了多孔碳化硅陶瓷对烟气的过滤性能.
The porous silicon carbide ceramics were surface modified with molten salts of anhydrous aluminum sulfate and sodium sulfate and the phase composition and microstructure after molten salt reaction were studied.The PM2.5 filtering performance of the porous silicon carbide ceramics before and after modification was tested.The results show that the acicular mullite whiskers with lengths of over ten microns and diameters of several hundred nanometers were produced by the reaction of the molten salts of aluminum sulfate and sodium sulfate with silicon carbide at 900 ℃.The mass concentration of PM2.5 in diesel smoke was decreased from over 280μg?m-3 to less than 150μg?m-3 after filtration by the molten salt modified porous silicon carbide ceramic,which was better than that by the unmodified porous silicon carbide ceramic (200 μg?m-3 ).The mullite whiskers can block the movement of the particulate matters in diesel smoke and make them precipitate between whiskers,resulting in the improvement of smoke filtering performance of the porous silicon carbide ceramics.
参考文献
| [1] | M.A. Bautista;J. Quispe Cancapa;J. Martinez Fernandez.Microstructural and mechanical evaluation of porous biomorphic silicon carbide for high temperature filtering applications[J].Journal of the European Ceramic Society,20117(7):1325-1332. |
| [2] | 李红伟;王伟;郭亚杰;耿刚强;金海云.造孔剂对多孔碳化硅陶瓷制备工艺和抗弯强度的影响[J].机械工程材料,2013(1):47-50. |
| [3] | 王伟;薛涛;金志浩;乔冠军.一种新型多孔SiC的制备与性能研究[J].无机材料学报,2008(1):109-113. |
| [4] | Jihong She;Jian-Feng Yang;Naoki Kondo;Tatsuki Ohji;Shuzo Kanzaki;Zhen-Yan Deng.High-strength porous silicon carbide ceramics by an oxidation-bonding technique[J].Journal of the American Ceramic Society,200211(11):2852-2854. |
| [5] | Youngseok Kim;Kyungseok Min;Jim Shim.Formation of porous SiC ceramics via recrystallization[J].Journal of the European Ceramic Society,201213(13):3611-3615. |
| [6] | Liu, R.;Liu, G.;Yang, J.;Jin, H.;Lu, Y.;Gu, W..Effect of removal of silicon on preparation of porous SiC ceramics following reaction bonding and recrystallization[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:9-14. |
| [7] | Wang, Bo;Zhang, Hui;Phuong, Hoang-Tuan;Jin, Feng;Yang, Jian-Feng;Ishizaki, Kozo.Gas permeability and adsorbability of the glass-bonded porous silicon carbide ceramics with controlled pore size[J].CERAMICS INTERNATIONAL,20152 Pt.A(2 Pt.A):2279-2285. |
| [8] | 梁汉琴;姚秀敏;黄政仁;刘学建.碳化硅陶瓷液相烧结时的液相生成过程[J].机械工程材料,2015(2):34-37. |
| [9] | Francesca Bortolani;Robert A. Dorey.Molten salt synthesis of PZT powder for direct write inks[J].Journal of the European Ceramic Society,201010(10):2073-2079. |
| [10] | Yang, Tao;Chen, Junhong;Li, Lidong;Chou, Kuo-Chih;Hou, Xinmei.Template free synthesis of highly ordered mullite nanowhiskers with exceptional photoluminescence[J].CERAMICS INTERNATIONAL,20158(8):9560-9566. |
| [11] | Pengyu Zhang;Jiachen Liu;Haiyan Du.Molten salt synthesis of mullite whiskers from various alumina precursors[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20101/2(1/2):447-451. |
| [12] | Grisel Corro;Umapada Pal;Edgar Ayala.Effect of Ag, Cu, and Au Incorporation on the Diesel Soot Oxidation Behavior of SiO2: Role of Metallic Ag[J].Topics in Catalysis,20131/8(1/8):467-472. |
| [13] | 李雪冬;朱伯铨.硫酸铝和氧化硅在硫酸钠熔盐中合成莫来石的动力学参数计算[J].硅酸盐学报,2008(4):498-502. |
| [14] | 李月明;王进松;廖润华;涂明林.熔盐法制备针状莫来石晶体的研究[J].人工晶体学报,2009(3):727-731. |
| [15] | Pengyu Zhang;Jiachen Liu;Haiyan Du.Influence of silica sources on morphology of mullite whiskers in Na_2SO_4 flux[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20091/2(1/2):580-584. |
| [16] | Wei Wang;Guiwu Liu;Guanjun Qiao.Moften Salt Synthesis of Muilite Whiskers from Silicon Carbide Precursor[J].Materials Science Forum,2012:299-302. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%