以高纯镁砂为骨料,通过原位合成、直接添加、复合添加锆酸钙三种方法制备了不同锆酸钙含量的镁质弥散型透气耐火材料,研究了锆酸钙添加量和添加方式对该耐火材料性能的影响。结果表明:随着直接添加方式下锆酸钙加入量的增加,试样的透气度、显气孔率和体积密度增大,线收缩率和强度减小,抗热震性能则先增后降,当锆酸钙质量分数达到9%时最高;在三种添加方式下,以原位合成方式添加锆酸钙试样的透气度、显气孔率、体积密度、线收缩率均最大,强度最低,而复合添加方式下试样的烧结性好,强度和抗热震性能最高。
The dispersed gas-permeable magnesia refractories with different calcium zirconate content were prepared by adding calcium zirconate with three methods of in-situ synthesis,direct addition and composite addition with pure magnesia as aggregates.The effects of the addition amount and addition method of calcium zirconate on the performance of the refractories were studied.The results show that with the increase of calcium zirconate amount by direct addition,the gas permeability,apparent porosity and bulk density of the samples increased and the linear shrinkage and strength decreased while the thermal shock resistance first increased and then decreased and reached the highest value with the calcium zirconate addition of 9wt%.Among the three addition methods,the gas permeability,apparent porosity,bulk density and linear shrinkage of the samples by in-situ synthesis were the highest and the strength was the lowest;while the sintering performance of that by composite addition was good and the strength and thermal shock resistance were the highest.
参考文献
[1] | 牛智旺;乔金贵;陈建华;罗焰;吴忠阳;刘华平.中间包透气上水口的研制与使用[J].耐火材料,2000(2):94-95. |
[2] | 战东平;姜周华;王文忠.耐火材料对钢水洁净度的影响[J].耐火材料,2003(4):230-232. |
[3] | 陶绍平;钟香崇.MgO基和Al2O3基耐火材料对钢中磷的影响[J].硅酸盐通报,2007(1):25-28. |
[4] | 游杰刚;张国栋;张玲;陈英;郑玉;蒋闯.镁质弥散型透气砖高温抗折强度的研究[J].硅酸盐通报,2012(1):140-144. |
[5] | 游杰刚;张国栋;金永龙;高配亮.二氧化硅对锆酸钙材料结构及性能的影响[J].人工晶体学报,2014(5):1280-1285. |
[6] | 孙静;黄传真;刘含莲;王随莲;邹斌;艾兴.稳定氧化锆陶瓷的研究现状[J].机械工程材料,2005(8):1-3,25. |
[7] | 陈德平;赵海雷;钟香崇;王俭.CaZrO3材料的制备及其显微结构[J].北京科技大学学报,2000(1):1-3. |
[8] | 王领航 .MgO-CaO-ZrO<,2>材料的制备与性能研究[D].西安建筑科技大学,2004. |
[9] | 钱忠俊 .MgO-ZrO<,2>-CaO原料的合成与应用研究[D].武汉科技大学,2002. |
[10] | 孔德玉;杨辉;陈桂华.高温推板砖抗热震稳定性研究[J].硅酸盐学报,2002(z1):109-111. |
[11] | 任耘.窑具材料显微结构与热震稳定性相关性研究[J].中国陶瓷,2001(05):20-22. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%