利用疲劳试验机和扫描电镜研究了在弱碱性介质(质量分数为3．0％的 KCl 溶液)中不同应力比R(0．1,0．3,0．5,0．7)对S135钻杆钢腐蚀疲劳行为的影响,并得到了该钻杆钢腐蚀疲劳裂纹扩展表达式和疲劳裂纹临界撕裂点的应力强度因子幅值ΔK 与R 的关系式.结果表明：随着R的增大,试样裂纹扩展临界撕裂点和最终撕裂点对应的ΔK 逐渐减小(R 和临界撕裂点的ΔK 值之间呈明显的线性关系),试样的腐蚀疲劳裂纹扩展速率增大,腐蚀疲劳相对寿命减小,裂纹开裂由疲劳条带扩展机制转化为解理扩展机制.
The influences of different stess ratios R(0.1,0.3,0.5,0.7)on the corrosion fatigue behaviour of S135 drill pipe steel in the weak alkali medium (3.0wt% KCl solution)were investigated by the fatigue tester and scanning electron microscope,and then the corrosion fatigue crack propagation rate expression and the relationship of R vs the stress intensity factor range ΔK at the fatigue crack critical tearing point were obtained.The results show that with the increase of R,theΔK at the crack critical and final tearing points of the specimen decreased gradually (the relationship between R and the critical tearing pointΔK was obviously linear);the corrosion fatigue crack propagation rate also increased while corrosion fatigue relative life decreased and the crack mechanism changed from stripe to cleavage fracture.
参考文献
| [1] | G. F. Miscow;P. E. V. de Miranda;T. A. Netto.Techniques to characterize fatigue behaviour of full size drill pipes and small scale samples[J].International Journal of Fatigue,20046(6):575-584. |
| [2] | 王荣;左冬声;雒设计.S135钻杆钢的单轴疲劳性能对比[J].机械工程材料,2012(04):50-53,61. |
| [3] | 宋全超;张建国;乙晓伟;王泓.有机玻璃裂纹扩展双参量驱动力模型[J].航空材料学报,2011(4):86-89. |
| [4] | 刘岗;郑子樵;杨守杰;戴圣龙;李世晨.2E12铝合金的疲劳性能与裂纹扩展行为[J].机械工程材料,2007(11):65-68,72. |
| [5] | 佘玲娟;郑子樵;钟警;林莉.6156铝合金疲劳裂纹的扩展速率[J].机械工程材料,2011(5):19-22,26. |
| [6] | B. L. Boyce;R. O. Ritchie.Effect of load ratio and maximum stress intensity on the fatigue threshold in Ti-6Al-4V[J].Engineering Fracture Mechanics,20012(2):129-147. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%