对厚度为8 mm的 Q890D高强钢中厚板对接焊接接头中的残余应力进行了有限元模拟，重点分析了接头中残余应力的分布和大小，并采用 X 射线衍射法和盲孔法进行了试验验证.结果表明：焊接接头中的纵向残余应力在起、收弧位置表现为压应力，中间部分表现为拉应力，拉应力的峰值为823．4 MPa；随着距焊缝距离增大，横向残余应力逐渐减小，且表现为拉应力；模拟结果与X射线衍射法的测试结果吻合得较好，误差为17．4％，证明了有限元模型的准确性.
Distribution and value of residual stress in welded joint of Q890D high strength steel medium and heavy plate of 8 mm thick were analyzed by finite element modeling,and X-ray diffraction method and blind-hole method were used to verify.The results show that,longitudinal residual stress in the welded joint was compressive stress in arc starting and arc stopping positions,the middle parts was tensile stress and the value of peak stress was 823.4 MPa.With the increase of distance from weld seam,transverse residual stress gradually decreased,and it showed tensile stress.The simulated results were in good agreement with the measured results from X-ray diffraction method,the error between them was 17.4%,this proved the accuracy of the finite element model.
参考文献
| [1] | 杜全斌;马成勇;彭云;张元杰;王华昆.热输入对Q890高强钢焊缝组织及性能的影响[J].材料科学与工艺,2013(5):143-148. |
| [2] | 童星;顾伟生;朱世根;白涛.304不锈钢薄壁焊管表面残余拉应力的测定及消除[J].机械工程材料,2012(02):80-82,99. |
| [3] | 王娜 .中厚板焊接残余应力测试的盲孔法研究[D].大连理工大学,2007. |
| [4] | 王超逸;吕丹;苏洪英;于秀蛾;杨成波;孙绍广.两种残余应力测定方法的研究和比较[J].理化检验：物理分册,2011(11):690-693. |
| [5] | 李益华;吴运新;龚海;李泉;张澄;王晓燕;吴中怀.应用X射线衍射法测定轴类工件中的残余应力[J].机械工程材料,2012(07):96-99. |
| [6] | 房元斌;蹤雪梅;张华清;孙波;占小红.中厚板多层多道焊优化技术研究[J].焊接技术,2016(3):5-8. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%