对异常开裂失效的220 kV断路器用60Si2CrVA钢弹簧的化学成分、显微组织、力学性能、断口形貌等进行了分析，以找到其失效原因。结果表明：弹簧呈脆性开裂特征，开裂原因是在弹簧磨簧过程中支撑圈表面产生异常高温，在随后水冷过程中形成了局部淬火马氏体组织。
In order to find the failure reason, the chemical composition, microstructure, mechanical properties and fracture morphology of unusual cracking failed 60Si2CrVA steel spring,which was used for 220 kV circuit breaker,were analyzed.The results show that the spring presented a brittle crack characteristic.The cracking reason was that the abnormal high temperature was produced on the surface of supporting ring during the spring grinding process and in the followed water cooling process formed the local quenching martensitic microstructure.
参考文献
| [1] | 刘高航;刘光明.工程材料与结构的失效及失效分析[J].国外金属加工,2006(1):6-9. |
| [2] | 张峥;陈再良;李鹤林.我国失效分析的现状与差距[J].金属热处理,2007(z1):49-52. |
| [3] | 申丽娟;程光辉;耿艳玲;薛佳鹏;赵天力.60Si2Mn弹簧钢失效机理分析[J].热加工工艺,2013(14):192-193. |
| [4] | 张正贵;李平;李姗姗;李战库;李梦琴;张瑞峰.60Si2MnA盘簧断裂失效分析[J].金属热处理,2014(12):156-158. |
| [5] | 蒋跃宁;何颜红.液化石油气罐车安全阀弹簧失效分析[J].化工机械,2009(2):154-156. |
| [6] | 金双峰,程鹏,姜膺,丁嘉怡.弹簧的失效分析与预防技术[C].2011年全国失效分析学术会议论文集,2011:140-144. |
| [7] | 刘克铭;马壮;张连勇;刘波.42CrMo钢磨削淬火强化层的显微组织和磨损性能[J].机械工程材料,2012(05):58-61. |
| [8] | 马壮;刘波;时海芳;刘克铭;孙方红.42CrMo钢的磨削淬火强化层的研究[J].兵器材料科学与工程,2011(5):26-28. |
| [9] | 秦松祥;肖冰;李曙生;宋正和;苏宏华;费振华;龚欢.40Cr钢磨削淬火层组织及其形成机理[J].机械工程材料,2007(12):24-26,29. |
| [10] | 尉雷;刘庆锁;杨婴;柴树平;王玮.65Mn钢弹性卡箍断裂失效分析[J].热加工工艺,2012(20):215-216,222. |
| [11] | 罗娟娟;史文;黄群飞;李麟.高马氏体量双相钢的组织与性能研究[J].钢铁,2008(4):84-88. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%