针对重庆钢铁集团近年来增加澳矿使用量后,炉渣中Al2O3含量的增加对炉渣流动性的不利影响,对重钢高炉的炉渣性能进行了试验研究。以重钢高炉现场渣为基础,利用旋转黏度计测试了Al2O3质量分数为12%、MgO质量分数为8%、TiO2质量分数为5%、碱度为1.07~1.50时,CaO-SiO2-Al2O3-MgO-TiO2渣系黏度变化情况;并测量了不同TiO2含量时炉渣黏度变化情况。研究结果表明:在当前碱度范围内,随着二元碱度增加,炉渣黏度降低,当二元碱度超过1.35时,黏度降低趋势变平缓;炉渣中加入适量TiO2能降低黏度,改善流动性。
More and more Australian iron ore had been consumed in Chongqing Iron and Steel Group Co., Ltd. in recent years and consequently the slag property had been changed, especially the increased value of Al2O3 in slag has defect on slag fluidity.The viscosity in CaO-SiO2-Al2O3-MgO-TiO2 slag that add chemical agents to industrial slags has been mea-sured at different R and the mass percent of Al2O3, MgO, TiO2 were fixed at 12%, 8%, 5%respectively. In addition the slags viscosity at different cotent of TiO2 has been measured. The results show that moderate content of TiO2 can reduce viscosity, and viscosity decreasing with basicity increasing at current scope, the viscosity decreasing trend flattens when basicity exceed 1.35.
参考文献
[1] | Muller J;Erwee M .Blast Furnace Control Using Slag Viscosi-ties and Liquidus Temperatures With Phase Equilibria Calcula-tions[J].Southern African Pyrometallurgy,2011,6(09):309. |
[2] | A. Kondratiev;E. Jak;P. C. Hayes .Predicting slag viscosities in metallurgical systems[J].JOM,2002(11):41-45. |
[3] | A. Shankar;M. Gornerup;A. K. Lahiri .Estimation of viscosity for blast furnace type slags[J].Ironmaking & Steelmaking: Products and applications,2007(6):477-481. |
[4] | Gladkii M M .Regulating the Operation of the Blast-Furnace by Pressure Drops[J].METALLURGIST,1961,5(08):355. |
[5] | Sunahara, K;Nakano, K;Hoshi, M;Inada, T;Komatsu, S;Yamamoto, T .Effect of high Al2O3 slag on the blast furnace operations[J].ISIJ International,2008(4):420-429. |
[6] | 李福民,吕庆,胡宾生,于勇,陶文.高炉渣的冶金性能及造渣制度[J].钢铁,2006(04):19-22. |
[7] | 何环宇,王庆祥,曾小宁.MgO含量对高炉炉渣粘度的影响[J].钢铁研究学报,2006(06):11-13,21. |
[8] | 张宗旺;周卫;赵晓骏.高Al2O3含量高炉炉渣的流动性能研究[A].北京:冶金工业出版社,2005:80. |
[9] | 沈峰满,郑海燕,姜鑫,魏国,温秋林.高炉炼铁工艺中Al2O3的影响及适宜w(MgO)/w(Al2O3)的探讨[J].钢铁,2014(01):1-6. |
[10] | Keiji SHIMODA;Koji SAITO .Detailed Structure Elucidation of the Blast Furnace Slag by Molecular Dynamics Simulation[J].ISIJ International,2007(9):1275-1279. |
[11] | Mysen B O .Relationships Between Silicate Melt Structure and Petrologic Processes[J].EARTH-SCIENCE REVIEWS,1990,27(04):281. |
[12] | 郭靖,程树森,赵宏博.基于结构理论的SiO2-CaO-MgO-Al2O3熔渣黏度的预报模型[J].钢铁研究学报,2013(08):6-11. |
[13] | Nakamoto M;Tsugawa Y;Kiyose A et al.Effect of TiO2 on the Viscosity of Molten Slag in SiO2-CaO-MgO System[J].Journal of High Temperature Society,2007,32(05):74. |
[14] | SohnⅡ;Wang W;Matsuura H et al.Influence of TiO2 on the Viscous Behavior of Calcium Silicate Melts Containing 17%Al2O3 and 10%MgO[J].ISIJ International,2012,52(01):158. |
[15] | Hyunsik Park;Jun-Young Park;Gi Hyun Kim .Effect of TiO_2 on the Viscosity and Slag Structure in Blast Furnace Type Slags[J].Steel Research International,2012(2):150-156. |
[16] | 穆红旺,张淑会,吕庆,孙艳芹.中性气氛下高铝中钛型高炉渣黏度的试验研究[J].钢铁,2012(06):18-21,50. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%