捣固焦由于成本低且性能指标较好而逐步推广使用，然而首秦高炉在使用捣固焦后出现了炉内压量关系紧张、炉况不顺等问题。为了了解这批焦炭的实际性能，进行了反应性试验、差热试验以及光学组织含量分析，结果表明：焦炭光学组织中镶嵌结构有抑制裂纹发展和缓解热膨胀的作用，而捣固焦的镶嵌组织含量较低，因此在高温和冲击受力的作用下更容易产生裂纹；分析6种焦粉失重曲线可以发现，同性组分ΣISO含量高的捣固焦粉从1000升高到1300℃过程中汽化反应失重率增加更快，在炉内可能引起的粒度降解更严重，从而造成炉况不顺。
Because of low cost and high performance index, the stamping coke had been gradually popularized and appli-cated. However, after using the stamping coke in the blast furnace of Shouqin, it appears several problems such as pressure instability and instable BF performance. In order to make out the actual properties of this batch of coke, the reactivity test, TG-DTA test and optical texture analysis were conducted. The results indicated some relations between optical texture con-tent and quality of cokes. The mosaic texture in the optical texture of coke had an effect on controlling the development of cracks and relieving thermal expansion. The content of mosaic texture in the stamping coke was lower, so it was more prone to generating the cracks in the condition of high temperature and impact. From the weight loss curves of six kinds of coke powder, it can be found that the gasification reaction rate of the stamping coke with highΣISO increased faster in the process of the temperature from 1 000 to 1 300℃. In that case, it is possible to cause more serious particle degradation, re-sulting in the instable BF performance.
参考文献
| [1] | 丁汝才,吴铿,尹晓莹,费三林,何海熙,韦少华.首秦1号高炉降低燃料比和提高喷煤比的工业实践[J].钢铁,2009(03):18-23. |
| [2] | 傅永宁.高炉焦炭[M].北京:冶金工业出版社,1995 |
| [3] | 周师庸.探讨现行高炉焦炭质量指标模拟性的积极意义[J].钢铁,2000(02):1-3. |
| [4] | 周师庸.高炉焦炭质量指标探析[J].炼铁,2002(06):22-25. |
| [5] | S. H. KRISHNAN;P. S. DASH;M. GUHA .Application of Binder in Stamp Charge Coke Making[J].ISIJ International,2004(7):1150-1156. |
| [6] | 马超,张建良,庞清海,祁成林.高温捣固焦与顶装焦抗碱性差异研究[J].燃料与化工,2012(05):25-26,28. |
| [7] | R. SHARMA;P. S. DASH;P. K. BANERJEE .Effect of coke micro-textural and coal petrographic properties on coke strength characteristics[J].ISIJ International,2005(12):1820-1827. |
| [8] | 杨敏.冶金焦气化反应前后光学组织的研究[J].燃料与化工,2003(05):241-244. |
| [9] | 王晓磊,郭治,曲思建,张飏,商铁成,王利斌.焦炭显微结构及矿物质存在下反应性变化规律探讨[J].洁净煤技术,2008(02):87-89. |
| [10] | 张代林,曾涛,李伟锋,王培珍,郑明东.煤焦显微结构特征与焦炭性质的关系[J].钢铁,2011(01):14-18. |
| [11] | 晁伟,张小明,马超,孙健,刘洋,徐荣广,李东涛.焦炭的微观结构与性能关系研究[C].第五届宝钢学术年会论文集,2013:1-5. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%