在脱磷剂种类和配比一定的条件下，借助微型烧结实验手段，研究了碱度、温度、配碳量和磷含量等因素对高磷钢渣气化脱磷率的影响规律。研究发现，碱度升高，钢渣气化脱磷率降低，温度升高，钢渣气化脱磷率升高；随着配碳量增加，钢渣气化脱磷率先升高后降低，磷含量增加，钢渣气化脱磷率升高，当磷含量达到一定水平后，磷含量对气化脱磷率的影响减弱，并最终确定了各因素的最佳状态。
In certain conditions of dephosphorization agent type and proportion, with the help of micro sintering experi-ment method, the basicity, temperature, carbon and phosphorus content on the influence of gasification dephosphorization rate of high phosphorus steel slag was studied. The studies have shown that increasing the alkalinity, gasification dephos-phorization rate of steel slag decreased, improving the temperature, gasification dephosphorization rate rose, with the in-creased amount of carbon in steel slag, the rate of gasification dephosphorization first increased and then reduced, increas-ing the phosphorus content, gasification dephosphorization rate increased,and when the phosphorus content reached a cer-tain level, the effect of phosphorus content on the gasification dephosphorization rate was weakened, and ultimately deter-mine the optimum state of each factor.
参考文献
| [1] | 李灿华.我国钢渣资源化利用趋势分析[J].武钢技术,2010(04):51-54. |
| [2] | 再协.2010钢铁行业运行情况及2011年展望[J].中国资源综合利用,2011(02):62-63. |
| [3] | 李小川. 2011年5月我国钢铁工业生产概况[J].经济分析, 2011(27):1.,2011. |
| [4] | 中国工程院.中国可持续发展矿产资源战略研究--综合卷[M].北京:科学出版社,2005.,2005. |
| [5] | 陈其慎,王高尚.世界铁矿石市场与中国铁矿石供需形势[C].矿床学研究面向国家重大需求新机遇与新挑战--第八届全国矿床会议论文集,2006:827-830. |
| [6] | 陈亮亮,刘养洁.世界铁矿资源分布对我国钢铁工业发展的影响[J].经济研究导刊,2010(05):35-37. |
| [7] | 陈津,侯向东,宋平伟,林原生.锰矿粉微波加热还原脱磷[J].过程工程学报,2008(z1):231-235. |
| [8] | 杨景玲,张宇,朱桂林,等.加快钢渣“零排放”,努力完成“十一五”规划节能减排的目标[J].冶金环境保护,2007(6):7.,2007. |
| [9] | Fukagai S, Hamano T,Tsukihashi F. Formation reaction of phos-phate compound on multi phase flux at 1 573 K[J]. ISIJ Interna-tional, 2007, 47(1):187.,2007. |
| [10] | Suito H, Inoue R. Behavior of phosphorous transfer from CaO-FetO-P2O5(-SiO2)slag to CaO particles[J]. ISIJ lntemational, 2006, 46(2):180.,2006. |
| [11] | 陈伟.转炉钢渣的处理和利用[J].湖南有色金属, 2000, 16(4):36.,2000. |
| [12] | Deo B, Halder J, Snoeijer B, et al. Effect of MgO and Al2O3 vari-ations in oxygen steelmaking(BOF)slag on slag morphology and phosphorus distribution[J]. Ironmaking and Steelmaking, 2005, 32(1):54.,2005. |
| [13] | 王书桓,吴艳青,刘新生,徐志荣,吕晓芳.硅还原转炉熔渣气化脱磷实验研究[J].钢铁,2008(02):31-34. |
| [14] | 王书桓,吴艳青,徐志荣,吕晓芳,张响,王春梅,刘太新.硅还原转炉熔渣气化脱磷热力学分析[J].炼钢,2008(01):31-34. |
| [15] | Morita K, Guo M, Oka N, et al. Resurrection of iron and phos-phorus resource in steelmaking slags[J]. Journal of Material Cy-cles and Waste Management, 2002(4):931.,2002. |
| [16] | 陈津,侯向东,宋平伟,林原生.锰矿粉微波加热还原脱磷[J].过程工程学报,2008(z1):231-235. |
| [17] | 邱礼有,江礼科 .窑法磷酸生产的旋窑制气试验研究[J].化学反应工程与工艺,1993,9(1):90.,1993. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%