为探讨KR脱硫渣的脱硫机理,利用现场取脱硫渣,通过炉渣淬火实验,对渣中矿相组成和硫在渣中分布进行研究与分析。研究结果表明:KR渣主要位于CaO-SiO2-CaF2-CaS四元系,渣中含有单一的CaS相、以CaO为主的CaO-CaF2-CaS相和以CaO、SiO2为主的CaO-SiO2-CaF2-CaS相,且CaS相中的硫含量明显高于其他2种矿相。通过统计渣相中CaS相的面积分数,并结合炉渣总的硫含量,得出渣相中的硫主要以单一的CaS形式存在。因此,通过提高渣相中CaS相的面积分数,可提高炉渣硫含量。

The phase and distribution of sulfur in KR desulfurization slag was analyzed by quenching experiment to inves-tigate the desulfurization mechanism of KR slag . It was found that KR slag was located in the four component system of CaO-SiO2-CaF2-CaS, which was consisted of the single phase of CaS、the multi-phase of CaO-CaF2-CaS and the multi-phase of CaO-SiO2-CaF2-CaS, and the sulfur content in CaS phase was apparently higher than the other two phases. Fur-ther, the sulfur in slag mainly existed in the form of calcium sulphide according to statistical analysis of area fraction for CaS phase and the total sulfur content in slag. The sulfur content in slag could be thus added by increasing the area frac-tion of CaS phase.

参考文献

[1] 李明晖,欧阳德刚,李具中,吴杰,邓品团,罗巍,朱善合,王海青.KR脱硫效果影响因素的水模实验研究[J].武钢技术,2009(04):28-30,60.
[2] 陈树国,刘宇,姜进强 .济钢KR铁水预处理工艺设计[J].山东冶金,2003,25
[3] 袁勇,何运顺,肖建华,容水.川威KR脱硫前渣研究[J].重庆科技学院学报:自然科学版,2012(01):115-117.
[4] 王进文,白登涛.KR法铁水脱硫工艺的探讨[J].南方金属,2011(06):12-14.
[5] 付中华,杨宁川,吴燕萍,胡燕,吴令.KR脱硫效果影响因素分析[J].工业加热,2013(01):57-59.
[6] 李凤喜,李具中,萧忠敏,曹维,王雪冬,陈清泉,张文辉.武钢二炼钢KR铁水脱硫生产实践[J].炼钢,2005(05):1-4,53.
[7] 韩宝,邓勇,胡淑霞.马钢300tKR铁水预处理生产实践[J].安徽冶金科技职业学院学报,2011(04):5-8.
[8] 戴超,徐熙.浦钢公司铁水KR脱硫工艺实践[J].钢铁,2010(12):92-94.
[9] 李宁,郭汉杰,宁安刚.关于KR脱硫工艺脱氧理论问题的研究[J].钢铁,2011(10):36-41.
[10] 陈俊孚,李海洋,沈武,刘守堂,孙伟,杨治争,朱万军.高效脱硫法在KR脱硫生产中的应用[J].炼钢,2012(02):7-9.
[11] 李胜超,廖利辉,庞建飞,余明红,邓品团.武钢KR脱硫工艺改进[J].钢铁研究,2013(04):39-42.
[12] 张龙强,田乃媛,徐安军.新建钢厂铁水预处理模式的选择[J].炼钢,2008(01):58-62.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%