利用热膨胀仪研究了合金元素硅和铬对C-Si-Mn-Nb系与C-Cr-Mn-Nb系超高强双相钢连续冷却相变规律的影响；采用单向拉伸试验，以及OM、SEM和TEM等方法对比研究了2种DP钢的组织性能与断口形貌。结果表明：硅元素能够提高Ac1和Ac3点温度，扩大两相区，促进铁素体相变，并能提高马氏体的回火稳定性，改善其形貌和分布；铬元素的添加导致了奥氏体中碳的分布不均匀，使得马氏体内部同时出现了孪晶与板条状精细结构，而且快冷过程中出现了残余奥氏体和马奥岛组织，部分马氏体会在时效过程中发生分解；两钢的抗拉强度均超过1000 MPa，伸长率超过15%，且含硅的双相钢各项力学性能均要优于含铬的双相钢。
The effects of Cr and Si on the transformation of C-Cr-Mn-Nb and C-Si-Mn-Nb ultra-high strength dual phase steels were analyzed by using thermal dilatometer. The microstructure properties and the fracture surfaces of the steels were tested by tensile tests,optical microscopy,scanning electron microscopy and transmission electron microscope. The results show that the addition of Si can increase the temperature of Ac1 and Ac3 ,enlarge the two phase region,promote the ferrite transformation,increase the aging stability of martensite and improve its morphology and distribution;the addi-tion of Cr leads to the uneven distribution of C in austenite,the appearance of lamellar and parallel twin microstructure, as well as the appearance of residual austenite and the M/A in the fast cooling stage and the decomposition of some mar-tensite in overaging stage. Although tensile strength and elongation of the two steels both exceed 1 000 MPa and 15%re-spectively,the comprehensive mechanical properties of DP steel containing Si are superior to that containing Cr.
参考文献
| [1] | 康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009 |
| [2] | 康永林,陈贵江,朱国明,宋仁伯.新一代汽车用先进高强钢的成形与应用[J].钢铁,2010(08):1-6,19. |
| [3] | 米振莉,段路昭,李志超,江海涛,代乐乐.连续退火温度对高硅双相钢组织及性能影响[J].钢铁,2013(09):54-57. |
| [4] | 董毅,韩斌,时晓光,徐鑫,刘仁东.冷却工艺对Si-Mn系热轧双相钢组织和性能的影响[J].钢铁,2011(10):66-69,74. |
| [5] | Nouri A;Saghafian H;Kheirandish Sh .Effects of silicon content and intercritical annealing on manganese partitioning in dual phase steels[J].Journal of Iron and Steel Research Internation-al,2010,5(17):44. |
| [6] | 陈连生,张健杨,田亚强,宋进英,魏英立,赵远.C-Si-Mn系双相钢锰配分行为及其对组织性能的影响[J].钢铁研究学报,2014(05):72-76. |
| [7] | 叶洁云,赵征志,汪志刚,赵爱民.1000 MPa级C-Si-Mn-Nb系冷轧双相钢的组织性能[J].材料热处理学报,2013(04):104-110. |
| [8] | HAN Qi-hang,KANG Yong-lin,ZHAO Xian-meng,L(U) Chao,GAO Lu-feng.Microstructure and Properties of Mo Microalloyed Cold Rolled DP1O00 Steels[J].钢铁研究学报（英文版）,2011(05):52-58. |
| [9] | 王健,房锦超,张玉文.热轧双相钢 DP600关键工艺技术[J].中国冶金,2014(11):42-45,49. |
| [10] | Son YI;Lee YK;Park KT;Lee CS;Shin DH .Ultrafine grained ferrite-marten site dual phase steels fabricated via equal channel angular pressing: Microstructure and tensile properties[J].Acta materialia,2005(11):3125-3134. |
| [11] | 徐刚.780MPa级冷轧双相钢的组织与性能[J].钢铁研究学报,2012(08):44-47. |
| [12] | 王笑天.金属材料学[M].北京:机械工业出版社,1987 |
| [13] | Nouri A;Saghafian H .Kheirandish. Effects of silicon content and intercritical annealing on manganese partitioning in dual phase steels[J].Journal of Iron and Steel Research Internation-al,2010,5(17):44. |
| [14] | 王科强,刘仁东,王旭,林利,郭金宇.缓慢冷却工艺对高强度冷轧双相钢组织性能的影响[J].钢铁研究学报,2012(02):44-48. |
| [15] | A. García-Junceda;F.G. Caballero;C. Capdevila;C. García de Andrés .Determination of local carbon content in austenite during intercritical annealing of dual phase steels by PEELS analysis[J].Scripta materialia,2007(2):89-92. |
| [16] | Lis J;Lis A K;Kolan C .Pressing and properties of C-Mn steel with dual-phase microstructure[J].Journal of Materials Process-ing Technology,2005,162/163:350. |
| [17] | U. F. Kocks;H. Mecking .Physics and phenomenology of strain hardening: the FCC case[J].Progress in materials science,2003(3):171-273. |
| [18] | 金光灿,赵征志,徐刚,赵爱民,刘光明.1 000 MPa热镀锌双相钢组织和断裂机理[J].北京科技大学学报,2009(10):1245-1249. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%