高强钢板在进入层流冷却前，因其宽度方向上的中部和边部初始温差过大，导致层流冷却后钢板出现双边浪缺陷。针对此问题，通过试验测量不同初始温差钢板层流冷却后长度方向的残余应力，以测量的残余应力作为边界条件，建立了钢板稳定性分析模型，运用解析方法求解出钢板屈曲失稳的临界残余应力。将试验测量的残余应力最大值和初始温差进行拟合，根据钢板屈曲失稳的临界残余应力求出临界初始温差约为40℃，这对高强钢板的生产有切实的指导作用。
Because of bilateral wave on high strength strip after laminar cooling for high temperature difference be-tween edge and central area,initial temperature difference experimental devices were built up to measure residual stress in the length direction under different conditions. Then,the model of strip stability analysis was built,and analytical method was used to calculate the critical residual stress when the buckling of strip happens. According to the critical re-sidual stress and fit result of initial temperature difference and residual stress,the critical initial temperature difference was calculated,which is 40℃and the result is important to guide the production.
参考文献
| [1] | 王澜;曹建国;贾生晖;曾彤.冷轧带钢板形屈曲变形失稳限的有限元分析[J].中南大学学报（自然科学版）,2007(6):1157-1161. |
| [2] | 陈银莉;余伟;苏岚;白冰.热轧带钢层流冷却过程中残余应力分析[J].材料热处理学报,2010(6):155-160. |
| [3] | 苏艳萍;杨荃;何安瑞;王晓东;边海涛.热轧带钢层流冷却过程中的热力耦合求解[J].重型机械,2007(4):30-34. |
| [4] | 万仁保.层流冷却过程中热轧带钢的应力及计算机仿真[J].热加工工艺,2015(5):151-153,156. |
| [5] | 韩斌;佘广夫;焦景民;张中平;刘相华;王国栋.热轧板带钢冷却过程中热力耦合计算及变形分析[J].钢铁,2005(4):39-42,56. |
| [6] | 朱冬梅;刘国勇;李谋渭;张少军.中厚板冷却过程中热残余应力的控制[J].北京科技大学学报,2008(8):947-951. |
| [7] | 苏艳萍;杨荃;何安瑞;王晓东;边海涛.ASP1700热轧层流冷却过程中影响板形变化的热应力求解[J].钢铁,2008(5):55-60. |
| [8] | 张鹏;程树森;常崇明;李积鹏;郑跃强.热轧带钢层流冷却过程温度场研究[J].钢铁,2014(10):51-57. |
| [9] | 余伟;卢小节;陈银莉;白冰.热轧带钢在常规层流冷却中温度不均匀性的有限元分析[J].钢铁,2011(4):44-48. |
| [10] | 程杰锋;唐广波;刘正东;董瀚;毛新平;戚培建;宋昕;谢利群;李烈军;陈学文.珠江钢厂CSP热连轧层流冷却热过程模拟研究[J].钢铁,2003(11):28-31. |
| [11] | 张清东;刘赟赟;周晓敏;邹玉贤;黄夏兰;彭俊.高温带钢的局部宽度内压屈曲及后屈曲分析[J].机械工程学报,2005(3):102-106. |
| [12] | 戴杰涛;张清东.冷轧薄板中浪板形缺陷的屈曲及后屈曲理论与轧试验研究[J].机械工程学报,2011(2):44-50. |
| [13] | 卿伟杰;杨荃.冷轧带钢整体和局部屈曲及后屈曲的有限元分析[J].北京科技大学学报,2000(4):377-380. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%