在连铸过程中，结晶器易结渣圈是造成铸坯产生缺陷的主要原因之一。对304不锈钢板坯连铸过程中结晶器保护渣原渣、距开浇60 min时的液渣和渣圈的化学组成、理化性能、结晶矿相以及渣圈形貌结构进行对比分析。结果表明，连铸过程中TiO2和Cr2O3从钢液进入液渣生成高熔点氧化物，使液渣和渣圈的完全熔化温度和黏度显著增大，碱度、转折温度降低。液渣与渣圈的物相以枪晶石和钙铝黄长石为主。高熔点相钙铝黄长石的大量析出以及TiO2和Cr2O3进入液渣使液渣黏度增大是渣圈形成并长大的重要原因。
Formation and growth of slag rim in continuous casting mold is one of the important causes to worse slab quality. In this article,the chemical ingredient,physical-chemical properties,crystallized mineralogical phases,composi-tion and structure of slag rim,original mold flux and mold flux for 304 stainless steel after 60 min from casting start were studied. The results show that TiO2 and Cr2O3 in molten steel moved into the mold flux and generated some oxides with high melting point during continuous casting process,during which the completely melting temperature and viscosi-ty of mold liquid flux and slag rim increased obviously,while the basicity and break temperature decreased. The mold liquid flux and slag rim were mainly composed of cuspidine and gehlenite. The precipitation of high-melting-point phase gehlenite and the increasing of mold flux viscosity caused by TiO2 and Cr2O3 are the main causes to form the slag rim in mold.
参考文献
| [1] | 王文学;王雨;迟景灏.不锈钢连铸坯表面缺陷与对策[J].钢铁钒钛,2006(3):63-68. |
| [2] | 范培耕;曹鹏军;徐启昆.奥氏体不锈钢半成品钢板表面缺陷成因分析[J].钢铁,2003(3):50-52,76. |
| [3] | 滕涛;陈银莉;赵爱民;周欢;汪淑英.304不锈钢冷轧薄板表面线缺陷的形貌[J].钢铁钒钛,2007(3):28-32,50. |
| [4] | 茅卫东.SUS304不锈钢表面抛光缺陷原因分析及改进措施[J].上海金属,2011(02):58-62. |
| [5] | 王新月;席常锁;卢军辉;胡志刚;胡进洲;杨海滨.影响板坯连铸产生渣圈的因素[J].炼钢,2010(2):53-56. |
| [6] | 闫威;陈伟庆;Carsten Lippold;郑宏光.无磁钢20Mn23AlV保护渣液渣和渣圈性能变化对连铸的影响[J].特殊钢,2013(1):45-48. |
| [7] | K.C. Mills;L. Yuan;R.T. Jones.Estimating the physical properties of slags[J].Journal Of The South African Institute Of Mining & Metallurgy,201110(10):649-658. |
| [8] | S.Sridhar;K.C.Mills.Break temperatures of mould fluxes and their relevance to continuous casting[J].Ironmaking & Steelmaking: Products and applications,20003(3):238-242. |
| [9] | J. A. Kromhout;C. Liebske;S. Melzer.Mould powder investigations for high speed casting[J].Ironmaking & Steelmaking,20094(4):291-299. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%