为研究退火工艺对冷轧中碳钢组织、织构演变以及力学性能的影响,利用OM、SEM、XRD、显微硬度计和万能试验机展开研究.结果表明,500℃保温时,以回复软化机制为主,被压扁的铁素体在保温30 min时才出现少许再结晶,保温10 min之后,显微硬度变化不明显,渗碳体以片层状为主;600℃保温时,其软化机制以再结晶为主,保温20 min时,仍存在部分未再结晶的变形铁素体晶粒,渗碳体片层以粒状为主,多偏聚于原珠光体区域,显微硬度急剧降低,保温30 min时再结晶完成;700℃保温10 min时铁素体再结晶基本完成,渗碳体为均匀的粒状分布,显微硬度变化较小;随退火温度升高以及保温时间的延长,γ织构强度减弱,而(110)<001>织构和γ'织构强度逐渐增强;当退火工艺为700℃保温10 min时,可以获得较好的强韧性组合.
参考文献
| [1] | 惠亚军;于洋;王林;王畅;陈斌;陈瑾.钛微合金化IF钢第二相粒子应变诱导析出行为[J].钢铁,2016(1):82-89. |
| [2] | C. Herrera;N. B. Lima;A. Ferreira Filho;R. L. Plaut;A. F. Padilha.Texture and mechanical properties evolution of a deep drawing medium carbon steel during cold rolling and subsequent recrystallization[J].Journal of Materials Processing Technology,20097(7):3518-3524. |
| [3] | Plaut, RL;Padilha, AF;Lima, NB;Herrera, C;Ferreira, A;Yoshimura, LH.Medium carbon steel deep drawing: A study on the evolution of mechanical properties, texture and simulations, from cold rolling to the end product[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,20091/2(1/2):337-341. |
| [4] | 于宏;田素贵;耿新.钢中渗碳体的冷变形特征及其作用[J].钢铁研究学报,2002(3):43-46. |
| [5] | Xiaodan Zhang;Andy Godfrey;Xiaoxu Huang.Microstructure and strengthening mechanisms in cold-drawn pearlitic steel wire[J].Acta materialia,20119(9):3422-3430. |
| [6] | 刘祥;倪自飞;姚利丽;薛烽;严木香;底华芳.冷变形过共析珠光体钢丝的微观组织演化[J].材料热处理学报,2015(8):181-185. |
| [7] | 崔瑞婷;金自力;闫波;张利博;郭冬青;曹晓明.基于CSP工艺稀土冷轧板罩式退火中组织织构演变[J].钢铁研究学报,2013(3):34-38. |
| [8] | 周敏;厉勇;刘荣佩;王春旭;黄顺喆;韩顺.新型二次硬化渗碳钢的高温塑性及热加工图[J].钢铁,2016(6):76-81,93. |
| [9] | 毛新平;孙新军;汪水泽.薄板坯连铸连轧流程钛微合金钢控制轧制技术[J].钢铁,2016(1):52-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%