首钢热轧汽车大梁钢冲压开裂原因分析

1.首钢技术研究院,北京100043

2.首钢技术研究院,北京100043

3.首钢迁安钢铁有限责任公司,河北迁安064404

4.首钢迁安钢铁有限责任公司,河北迁安064404

5.首钢技术研究院,北京100043

6.首钢技术研究院,北京100043

Analysis on the Reasons of Stamping Cracks in Hot-rolled Automobile Beam Steel Produced by Shougang

探讨了首钢热轧汽车大梁钢510L、S610L和S750L在应用过程中出现开裂的原因.利用光学显微镜(OM)、扫描电镜(SEM)对牌号为510L、S610L和S750L的开裂试样进行了微观组织分析.结果表明:表面铁皮压入、严重的中心偏析带以及晶界较为粗大的析出物等均可导致热轧汽车大梁钢成型开裂.

[1]	许可.影响钢板冲压成形极限因素的研究[J].机电产品开发与创新,2007(04):20-22.
[2]	Hai-Long YI;Lin-Xiu DU;Guo-Dong WANG;Xiang-Hua LIU .Development of a Hot-rolled Low Carbon Steel with High Yield Strength[J].ISIJ International,2006(5):754-758.
[3]	HERMAN J C;DONNAY B;LEROY V .Precipitation kinetics of microalloying additions during hot-rolling of HSLA steels[J].ISIJ International,1992,32(06):779.
[4]	M. CHARLEUX;W.J. POOLE;M. MILITZER .Precipitation Behavior and Its Effect on Strengthening of an HSLA-Nb/Ti Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(7):1635-1647.
[5]	M. GOMEZ;S. F. MEDINA;A. QUISPE .Static Recrystallization and Induced Precipitation in a Low Nb Microalloyed Steel[J].ISIJ International,2002(4):423-431.
[6]	赵楠,穆海玲,周丽萍,曹博蕊,赵建国.BM510汽车大梁钢冷弯开裂原因分析[J].机械工程材料,2008(11):72-74.
[7]	方圆,阳代军,张宏艳,艾矫健.汽车大梁钢510L冲压开裂原因分析[J].热加工工艺,2012(03):169-170,172.
[8]	赵培林,孙新军,雍岐龙,路峰.超高强度热轧钢板冷冲压开裂原因及分析[J].金属热处理,2012(07):122-126.
[9]	雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006
[10]	郑东升,朱伏先,李艳梅,刘勇,余光夫.控轧控冷工艺对汽车大梁板组织及冷弯性能的影响[J].中国冶金,2009(05):17-20.

上一张下一张

计量

作者相关

文章评分