从坩埚选择、试样称取量、升温速率等方面摸索了差示扫描量热法(DSC)测试非晶材料 Fe78 Si9 B13居里温度的最佳试验条件,分析了不同升温速率对测试结果的影响,同时与该材料晶化温度、In(标准物质)的熔点随升温速率的变化情况进行了对比分析.研究结果表明:该材料的 DSC 曲线上居里转变过程对应的热信号表现为一个抖动.不同条件下测得的居里温度为399~402℃,与 Hall 效应法测试结果基本一致.最佳的试验条件是:Al坩埚、试样称取量6 mg 左右、20 K/min.在升温速率不小于10 K/min 时可以得到居里转变信号,与该材料晶化温度受热滞后影响而明显随升温速率增大而增大的情况不同,由于居里转变过程相变潜热较小,居里温度测试结果基本不受热滞后的影响.

Determination of Curie temperature of amorphous alloy Fe78 Si9 B1 3 by differential scanning calorimetry was researched from the choices of crucibles,masses of the sample and heating rates,and then the optical test conditions were obtained.The relationship of Curie temperature of amorphous alloy Fe78 Si9 B1 3 with heating rates was analyzed and compared simultaneously with the relationships of crystallization temperatures of Fe78 Si9 B1 3 , melting temperature of In (standard material used for thermal analysis)with the heating rates.The results show that the heat signal of the Curie transition shows a little wave in the DSC curves.The Curie temperature obtained at different test conditions are about from 399 ℃ to 402 ℃,which are equivalent to the results obtained by the methods according to Hall effect.The best conditions are as follows:Al crucibles,mass of about 6 mg,heating rate of 20 K/min.It is found that the Curie signal can be obtained only as heating rates bigger than 10 K/min and the results are not affected obviously by the heating rates when they are increased because of the low heat as no thermal hysteresis affect the results,while the results of crystallization temperatures increase obviously for the thermal hysteresis.

参考文献

[1] 詹文山.非晶态磁性材料居里温度的测量[J].物理,1985(07):418.
[2] 张亮;李德仁;宋恩猛;卢志超;周少雄.非晶配电变压器铁芯的热处理工艺[J].钢铁研究学报,2012(4):39-41.
[3] 高振;郭金花;倪晓俊;李德仁;卢志超.Fe基块体非晶合金的结构转变及其对力学性能的影响[J].钢铁研究学报,2010(4):35-38.
[4] 李红;李艳萍;谢琰军;高光洁子;况春江.基线修正在非晶合金晶化动力学研究中的应用[J].物理测试,2015(3):8-11.
[5] 陆曹卫;张俊峰;李德仁;卢志超;周少雄.非晶态磁性材料热电阻及居里温度的测量[J].物理测试,2003(6):28-30.
[6] 李红;孙克;李艳萍;石毅;郭金花;卢志超.Fe80Si9B11非晶合金薄带热膨胀特性和结构弛豫分析[J].金属功能材料,2010(1):4-7,12.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%