后期渗氮工艺是一种低温板坯加热生产技术，广泛应用于取向硅钢生产企业。通过金相＋ODF织构分析对工艺各阶段组织进行研究。实验结果表明：热轧及常化织构板沿板厚方向分布不均匀，{110}＜001＞织构在距热轧板表面1/4厚度处分布最强；冷轧板织构主要是α线和γ线织构；脱碳退火后α线织构大量减弱，{111}＜112＞织构得到加强，而渗氮后织构变化不明显。二次再结晶组织大晶粒内部出现少量小尺寸的孤岛小晶粒，{001}＜100＞位向孤岛小晶粒是 Goss晶粒无法吞并的。
The nitriding technology is one of slab low reheating temperature technology,and then is widely used in electrical steel production enterprises.The microstructure evolution was studied by metallographic analysis and ODF method.The results show that textures of the hot-rolled and normalized sheets reveal uneven distribution in thickness direction,and {110}<001> texture of hot rolled sheet is the strongest on the 1/4 thickness distribu-tion.The cold-rolled textures are mainlyα-fiber andγ-fiber.After decarburizing annealing,α-fiber texture decrea-ses dramatically,and {111}<112> texture is strengthened,and nitriding texture is not changed.A few small is-land grains appears in the secondary recrystallization grains,the small grain of {001}<100> texture cannot be swallowed by Goss of grain.
参考文献
| [1] | Chun-Chih Liao;Chun-Kan Hou.Effect of nitriding time on secondary recrystallization behaviors and magnetic properties of grain-oriented electrical steel[J].Journal of Magnetism and Magnetic Materials,20104(4):434-442. |
| [2] | 孙颖;李军;赵宇;喻晓军;连法增.采用低温板坯加热工艺生产的取向硅钢中抑制剂的研究[J].钢铁,2009(5):64-67. |
| [3] | 吴忠旺;赵宇;李军;李波.低温取向硅钢热轧析出物与织构的研究[J].金属功能材料,2011(4):1-5. |
| [4] | 吴忠旺;李军;赵宇;李波.后天抑制剂获得法制取向硅钢析出物的转化规律[J].钢铁研究学报,2011(12):45-48. |
| [5] | 王若平;黎世德;方泽民;毛炯辉;李平和;许光.低温热轧高磁感取向硅钢板常化组织及析出相研究[J].金属热处理,2009(6):9-14. |
| [6] | 何忠治.电工钢的现状与展望[J].中国冶金,2001(04):14-16. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%