研究了α＋γ双相区热处理对430铁素体不锈钢热轧板显微组织和力学性能的影响，并与工业罩式炉退火后的热轧板显微组织和力学性能进行了对比分析。结果表明：在双相温度区间对430不锈钢热轧板进行热处理，分割了热轧板轧向的条带状组织，抑制了聚集组织的形成。与常规罩式炉退火工艺相比，双相区热处理显著提高了430不锈钢热轧板的伸长率，降低了屈服强度和硬度，有利于改善最终冷轧产品的冲压性能和抗起皱性。
Effect of heat treatment in ferrite and austenite phase field on microstructure and properties for 430 stain-less steel hot rolled sheets was investigated.Also its microstructure and properties were compared with that of the hot rolled sheets after annealing in the industrial batch annealing furnace.The results showed that heat treatment in dual phase temperature range for 430 stainless steel hot rolled sheets could split banded structure along the roll-ing direction and inhibit the formation of aggregate structure.Compared with the conventional batch annealing process,dual phase region heat processing can significantly increase the elongation of 430 stainless steel hot rolled sheets and lower the yield strength and hardness.It is proved that dual phase region heat processing is also benefi-cial to improving the forming performance and wrinkle resistance of final cold rolled sheets.
参考文献
| [1] | 刘海涛;杜伟;谢胜涛;刘振宇;王国栋.初始凝固组织对Cr17铁素体不锈钢组织、织构及成形性的影响[J].钢铁研究学报,2008(10):32-35,62. |
| [2] | 杜伟;江来珠;余海峰;孙全社.铁素体不锈钢的冲压性[J].宝钢技术,2012(6):66-76. |
| [3] | 杜伟;OLIVEIRA;Mariana P.;张伟.退火温度对铁素体不锈钢组织织构和深冲性的影响[J].宝钢技术,2013(4):6-11. |
| [4] | 邬珠仙;李茂君;张朝波;李东波.罩式退火对430铁素体不锈钢成型性及抗起皱性的影响[J].金属热处理,2013(5):96-100. |
| [5] | 陈思悦;徐京;张鑫;杨弋涛.退火温度对铁素体不锈钢热轧板组织与性能的影响[J].金属热处理,2013(2):102-105. |
| [6] | 刘海涛;高飞;马东旭;刘振宇;王国栋.高纯Cr17铁素体不锈钢热轧板退火温度对冷轧退火板成形性能的影响[J].钢铁,2010(8):75-79. |
| [7] | 吕庆功;陈光南;周家琮;唐历.深冲钢板的主要织构对塑性应变比的影响[J].钢铁研究,2000(5):40-43. |
| [8] | Yoshihiro YAZAWA;Mineo MURAKI;Yasushi KATO;Oasmu FURUKIMI.Effect of Chromium Content on Relationship Between r-value and {111} Recrystallization Texture in Ferritic Steel[J].ISIJ International,200310(10):1647-1651. |
| [9] | Yoshihiro Yazawa;Yoshihiro Ozaki;Yasushi Kato;Osamu Furukimi.Development of ferritic stainless steel sheets with excellent deep drawability by (111} recrystallization texture control[J].JSAE review,20034(4):483-488. |
| [10] | Jun-ichi HAMADA;Yoshinori MATSUMOTO;Fumio FUDANOKI.Effect of Initial Solidified Structure on Ridging Phenomenon and Texture in Type 430 Ferritic Stainless Steel Sheets[J].ISIJ International,200312(12):1989-1998. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%