莱钢特钢事业部新区采用铁水+废钢→100 t 电炉→双工位 LF→双工位 VD→圆坯连铸(650 mm)→步进式加热炉→950轧机轧制的流程生产高压锅炉管钢12Cr1MoV,通过优化冶炼工艺、调整精炼渣系、强化保护浇铸等措施,克服了12Cr1MoV 钢在实际生产中的困难,使12Cr1MoV 钢的化学成分、低倍以及非金属夹杂物评级等各项指标均满足用户要求。
The high pressure boiler tube steel 12Cr1MoV was produced with the path of hot metal+scrap → 100 t EAF→double LF→ double VD→ round billet continuous casting(section 650 mm),in the special steel division new district of Laiwu Steel.The difficulties that existed in the actual production of 12Cr1MoV can be overcame with the methods of the reinforcement smelting process,adjusting the refining slag,strengthen protective casting and so on. So the chemical composition,low power structure,non-metallic inclusions rating and other indicators of the 12Cr1MoV meet the customers requirement.
参考文献
[1] | 寄海明.电站锅炉管用钢15CrMoG的生产实践[J].特殊钢,2012(05):32-34. |
[2] | 李法兴.50 t EAF-LF(VD)-CC流程开发4130钢φ350 mm连铸圆坯的生产实践[J].特殊钢,2013(05):25-27. |
[3] | 李代钟 .钢中硫化物球化和对钢性能的影响[J].炼钢,1992(2):97.,1992. |
[4] | 蒲学坤,李桂军.时速200km钢轨钢中B类夹杂物控制技术[J].炼钢,2005(03):26-28. |
[5] | 杨振国,刘青,王彬,石荣山.50t超高功率电弧炉冶炼工艺优化[J].炼钢,2012(06):1-6,10. |
[6] | 王文军,郝宁,刘金刚,李永东,朱志远,孙硕猛.X80管线钢精炼过程夹杂物研究[J].中国冶金,2010(09):17-21,33. |
[7] | 缪新德,徐国庆,陈情华,赵晗.GCr15钢中大颗粒夹杂(DS类)的生成原因分析[J].炼钢,2007(02):21-24. |
[8] | 唐海燕,李京社,刘亮,高锦国,温德松,张露.高压锅炉钢的非金属夹杂物研究[J].炼钢,2008(04):26-29. |
[9] | 邹长东,耿涛,周彦召,赵家七,丁振涛,皇祝平.沙钢管线钢LF精炼的低成本深脱硫工艺[J].钢铁,2012(11):36-40. |
[10] | 官常忠.电站锅炉管用钢T91脱磷、去硫研究[J].特钢技术,2002(02):35-39. |
[11] | 董金武,刘洪波,高龙永,张松龄.降低连铸板坯表面纵裂纹的生产实践[J].山东冶金,2006(06):13-15. |
[12] | 王贞,刘静,鲁修宇,邓照军.热处理工艺对12Cr1MoV钢组织性能的影响[J].热处理技术与装备,2012(02):10-14. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%