采用不同的平整工艺对连续退火780 MPa 级别的冷轧双相钢进行平整试验，研究了平整伸长率对连续退火780 MPa 级别双相钢力学性能的影响，并建立了平整伸长率与780 MPa 级别双相钢力学性能的函数关系模型。研究表明：随着平整伸长率的提高，780 MPa 级别双相钢的屈服强度提高，抗拉强度保持不变，同时均匀伸长率和总伸长率均有所下降。
The tensile properties of 780 MPa grade cold-rolled continuous annealed dual phase steel were investigated under different temper rolling reductions.The function relationships between temper rolling reduction and the ten-sile properties were founded.The results indicate that with the increase of the temper rolling reduction,the yield strength of the steel increases simultaneously,while the ultimate tensile strength remains the same.In addition,the uniform elongation and total elongation of the steel decrease slightly.
参考文献
| [1] | 朱晓东,俞宁峰.平整对微Ti处理各向同性钢板的力学性能的影响[J].钢铁,2004(11):57-59. |
| [2] | 唐荻;田德新 .退火温度及平整量对 03Al 钢板组织性能的影响[J].钢铁,1999,34(3):47. |
| [3] | MA Q L;WANG D C;LIU H M et al.Effect of temper rolling on tensile properties of low-Si Al-killed sheet steel[J].Journal of Iron and Steel Research,International,2009,16(3):64. |
| [4] | FANG X;FAN Z;RALPH B.Effect of temper rolling on tensile properties of C-Mn steels[J].Materials Science and Technology,2002(18):285. |
| [5] | Hoggan E J;Scott R I;Barnett M R.Mechanical prop-erties of tension levelled and skin passed steels[J].Journal of Materials Processing Technology:International,2002(125/126):155. |
| [6] | 康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009 |
| [7] | 罗青,赵征志,徐刚,赵爱民,金光灿,刘光明.退火温度和平整对冷轧热镀锌双相钢组织和性能的影响[J].钢铁研究学报,2009(10):33-37. |
| [8] | 许云波,侯自勇,陈礼清,胡淑娥,孙卫华,王国栋.1000MPa级经济型高韧性工程机械用钢的研究开发[J].中国冶金,2013(04):27-30. |
| [9] | Sodjit S;Uthaisangsuk V.Microstructure based prediction of strain hardening behavior of dual phase steels[J].Materials and Design,International,2012(41):370. |
| [10] | 王豫,斯松华.高锰钢加工硬化规律和机理研究[J].钢铁,2001(10):54-56. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%