针对ML20MnTiB生产的10.9级扭剪型钢构螺栓紧固轴力标准偏差大的问题进行了试验分析,通过进行螺母的磷皂化试验和螺栓热处理试验,表明螺母表面润滑状态、螺栓热处理工艺都影响紧固轴力检验结果,但不是造成紧固轴力标准偏差大的主要原因.通过更换新的车刀,将螺栓尾部凹槽位置螺栓直径由13.9减小为13.6 mm,凹槽底部曲率半径由0.17增大为0.5 mm,使紧固轴力平均值由176降低为167 kN,同时标准偏差由17.4降低为15.5以下,解决了紧固轴力标准偏差大的问题.
For the problem of excess tight axle strength standard deviation of ML20MnTiB 10.9S torshear type bolt set used for steel structure, the phosphating and saponification experiment of nuts and the heat treatment experiment of bolts were carried out.The results showed that the lubrication condition of nut and the heat treatment process of bolt influenced the tight axle strength, but they were not the primary cause.After changing the lathe tool, the diameter of bolt tail groove reduced from 13.9 mm to 13.6 mm, and the radius of curvature of bolt tail groove enlarged from 0.17 mm to 0.5 mm.In consequence, the average of tight axle strength reduced from 176 to 167 kN, and the standard deviation of tight axle strength was reduced from 17.4 to 15.5 below.
参考文献
| [1] | 杨瑞;张鹏飞;程季青;房昺;赵建军.高强度螺栓新型水基薄膜润滑剂应用研究[J].铁道建筑,2012(9):141-143. |
| [2] | 黄传辉;何绍华.磷化-皂化处理27SiMn钢的摩擦磨损性能研究[J].润滑与密封,2012(5):57-59,64. |
| [3] | 王鸿利.影响盘条表面处理质量的主要因素[J].金属制品,2008(03):10-12. |
| [4] | 王家安;赵振铎;王丽君.中温锌系磷化膜及皂化膜的组织结构研究[J].材料保护,2007(1):8-9,27. |
| [5] | 倪晓臣 .回火工艺对W6Mo5Cr4V2高速钢扭转性能影响研究[D].武汉理工大学,2010. |
| [6] | 卢峰;康健;王超;王昭东;王国栋.回火温度对Q960级高强结构钢组织及力学性能的影响[J].钢铁,2012(2):92-95. |
| [7] | 段贵生.含硼高强度冷镦钢ML20MnTiB组织性能控制[J].炼钢,2009(03):16-18,73. |
| [8] | 高玉魁;姚枚.化学热处理对40Cr钢表象疲劳极限影响的定量化研究[J].航空材料学报,2002(4):21-25. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%