为了研究高效合金烘烤在转炉炼钢中的应用,对高效合金烘烤装置在转炉炼钢生产中的应用进行了实践研究.结果表明,对比传统合金烘烤方式,高效合金烘烤装置可在2~4 h内将15 t铁合金升温至400~600 ℃,进而有效去除铁合金内的结晶水.当铁合金实际温度达到450 ℃时,可将钢中氢质量分数降低至0.000 150%以下,同时出钢温度降低20.31 ℃,转炉终点碳质量分数提高0.027%,脱氧剂消耗降低20%.在满足洁净钢生产的同时,可降低生产成本.
To study the application of efficiency alloy baking in converter steelmaking,the efficient alloy baking device was applied in the production of converter steelmaking.Results showed that compared to the traditional alloy baking method,the high alloy baking device can heat 15 t ferroalloy to 400-600 ℃ within 2-4 hours,which can effectively remove the water of crystallization in ferroalloy.When the actual temperature of ferroalloy reached 450 ℃,the hydrogen mass fraction in steel can be reduced to below 0.000 150%,the tapping temperature can reduce by 20.31 ℃,the converter end-point carbon mass fraction can increase by 0.027%,and the consumption of deoxidizer can reduce by 20%.Therefore,it can decrease the production cost,while meeting the production of clean steel.
参考文献
| [1] | 李峰.钢中氢的危害及防范措施[J].江苏冶金,2004(02):6-8. |
| [2] | 王俊凯.钢中氢含量影响因素分析[C].第十五届全国炼钢学术会议论文集,2008:573-580. |
| [3] | 牛莲山;周景兰;李盆业;穆建忠.合金烘烤炉的技术改造[J].工业炉,2008(6):48-50. |
| [4] | 黄建军;张新文;周伟;杜志明.37Mn-1铸坯表面气孔缺陷分析与研究[J].中国冶金,2012(02):19-24. |
| [5] | 昝娜;丁桦;骆小鹏;唐正友;BLECK Wolfgang.晶粒尺寸对高锰奥氏体TWIP钢氢脆行为的影响[J].中国冶金,2016(1):23-30. |
| [6] | 降低转炉出钢温度的综合措施[J].中国冶金,2011(8):43-45,54. |
| [7] | 巨建涛;张敏娟;鲁慧慧;张朝晖.LF精炼过程中钢液氢含量的变化[J].钢铁,2011(10):32-35. |
| [8] | 曲乃斌.铁合金控制系统的研究与应用[C].工业自动化应用实践（全国第三届工业炉窑自动控制学术会议暨第五届炼钢、连铸和轧钢自动化学术会议：论文专辑）,2002:119-123. |
| [9] | 辛彩萍;岳峰;田罗林.硬线钢用盘条中夹杂物的调查[J].中国冶金,2015(8):10-14. |
| [10] | 战东平;张慧书;姜周华.含钙钡合金脱氧和非金属夹杂物控制技术研究[J].中国冶金,2006(10):25-28. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%