以柠檬酸为螯合剂,采用沉淀法制备了稀土Tb3掺杂的ZnWO4绿色荧光粉前驱体.通过差热分析(DTA)、热重分析(TG)、X射线衍射(XRD)等手段对产物进行了表征.结果表明,当退火温度低于700℃时,得到的样品为非晶态,而高于850℃退火处理后为单斜结构.使用荧光分光光度计研究了Tb3+在ZnWO4基质中的发光性质.结果显示,ZnWO4∶Tb3+样品在544 nm波长光的监测下于200～300 nm处出现由W→O及Tb→O跃迁共同作用产生的重叠激发峰和系列Tb3的f-f跃迁锐峰,其中位于488 nm处的激发峰非常显著,对应于Tb3的7F6→5D4跃迁.说明该法制备的荧光粉ZnWO4∶Tb3+能够被蓝光有效激发,可以与广泛使用的蓝光LED芯片的输出波长相匹配.在488 nm波长光的激发下观察到ZnWO4粉末中Tb3+的544 nm(5D4→7F5)强的特征发射,说明ZnWO4∶Tb3粉末可作为白光LED的绿色补偿荧光粉.当以267 nm激发ZnWO4∶Tb3+时,有宽的WO42-特征发射峰和Tb3的5D4→7F6及5D4 →7F5跃迁产生的发射峰,随着Tb3掺杂浓度的增加,WO42-的特征发射强度逐渐降低,而Tb3+的5D4→7F5跃迁强度增大,表明Tb3+与WO42-之间有能量转移.
参考文献
| [1] | Zhao, M.;Li, G.;Li, L.;Yang, L.;Zheng, J. .Structures and polymorph-sensitive luminescence properties of BiPO _4/Eu grown in hydrothermal conditions[J].Crystal growth & design,2012(8):3983-3991. |
| [2] | 尚淑娟,袁曦明,王娟娟,王永钱.彩色PDP荧光粉的发展现状与制备方法[J].稀土,2010(03):82-86. |
| [3] | Lee, HJ;Kim, KP;Hong, GY;Yoo, JS .The effect of flux materials on the physical and optical properties of Eu3+-activated yttrium oxide phosphors[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2010(6):941-946. |
| [4] | 冯春燕,孟媛,刘小丽,王敬贤,杨琳.微波场作用下白光LED用绿色荧光粉Ca3Sc2Si3O12：Ce的快速合成及其发光特性[J].稀有金属,2013(01):87-91. |
| [5] | 任新光,狄卫华.BaAl12O19：Mn2+和YPO4：Tb3+共混对等离子绿色发光体发光性能的改善[J].发光学报,2010(06):826-830. |
| [6] | 朱国贤,陈毅昭,连洪州,刘应亮.KZnF3∶Ce,Tb的溶剂热合成及光谱性质[J].无机化学学报,2012(01):8-12. |
| [7] | 莎仁,李霞,王喜贵.ZrO2：Tb3+纳米晶的离子交换法制备及其发光特性[J].无机化学学报,2009(05):844-848. |
| [8] | Xueyan Wu;Hongpeng You;Hongtao Cui .Vacuum ultraviolet optical properties of (La, Gd)PO_4:RE~3+(RE=Eu, Tb)[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2002(9):1531-1538. |
| [9] | Wang, ZL;Quan, ZW;Jia, PY;Lin, CK;Luo, Y;Chen, Y;Fang, J;Zhou, W;O'Connor, CJ;Lin, J .Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles[J].Chemistry of Materials,2006(8):2030-2037. |
| [10] | 莎仁,吴红英,王喜贵.Tb3+在燃烧法制备的CaLaAl3O7粉体中的发光性能[J].无机化学学报,2008(08):1331-1334. |
| [11] | M. Mancheva;R. Iordanova;Y. Dimitriev .Mechanochemical synthesis of nanocrystalline ZnWO_4 at room temperature[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2011(1):15-20. |
| [12] | 张晓薇,曹丽云,黄剑锋,刘一军,李佳.棒状ZnWO4纳米晶的合成及其光催化性能[J].无机材料学报,2012(11):1159-1163. |
| [13] | 王金颖,黄妙良,钟起权,林建明,吴季怀.ZnWO4纳米晶光催化剂的制备及表征[J].人工晶体学报,2009(01):64-70. |
| [14] | 杨魁胜,白旭,高艳敏,翟海青,曹阳.ZnWO4：Er3+,Yb3+纳米棒的制备及发光性能[J].无机化学学报,2010(06):1078-1082. |
| [15] | 蒋彩娜,王荣芳,何涛,周立亚.SiO2@ZnWO4：Eu3+红色荧光粉的制备及其发光性质研究[J].稀土,2012(05):87-90. |
| [16] | 曹广胜,季佳秀,王洪伟,董承武.Cd2+掺杂ZnWO4纳米棒的合成和光致发光性能研究[J].无机化学学报,2009(07):1217-1220. |
| [17] | 高永毅,占世平,钟慧.Ce3+对YPO4∶Tb3+,Ce3+微米球的发光调制及Tb3+与Ce3+间的能量传递[J].中国有色金属学报,2012(12):3562-3567. |
| [18] | 赵文玉,樊彬,李松波,张国斌,戴亚堂.绿色荧光粉Gd2Ba3B3O12：Tb3+的发光性能研究[J].光谱学与光谱分析,2011(03):617-620. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%