为建立剩余刚度与材料损伤量及剩余寿命的关系,将纤维增强树脂复合材料(FRP)层合板在拉-拉疲劳载荷作用下的失效模式划分为纤维间破坏、纤维随机断裂与分层3种类型,分析不同失效模式与剩余刚度退化量的定量关系,提出一个集成各失效模式影响的剩余刚度退化复合模型.该模型适用于占寿命绝大多数比例的Ⅰ、Ⅱ阶段,避免了Ⅲ阶段刚度降不确定性的影响.剩余刚度退化曲线按时间尺度归一化,消除了试件个体分散性影响,分散性显著降低.对4种E-glass/Epoxy玻璃纤维复合材料层压板与3种AS-4/聚醚醚酮(PEEK)碳纤维复合材料层压板的疲劳试验结果进行了统计分析,表明本文模型适于精确描述复合材料的剩余刚度下降规律.
参考文献
[1] | Joris Degrieck;Wim Van Paepegem.Fatigue damage modeling of fibre-reinforced composite materials: Review[J].Applied Mechanics Reviews: An Assessment of the World Literature in Engineering Sciences,20014(4):279-300. |
[2] | Fathollah Taheri-Behrooz;Mahmood M. Shokrieh;Larry B. Lessard.Residual stiffness in cross-ply laminates subjected to cyclic loading[J].Composite structures,20083(3):205-212. |
[3] | 翟洪军;姚卫星.纤维增强树脂基复合材料的疲劳剩余刚度研究进展[J].力学进展,2002(1):69-80. |
[4] | 姚卫星;宗俊达;廉伟.监测复合材料结构剩余疲劳寿命的剩余刚度方法[J].南京航空航天大学学报,2012(5):677-682. |
[5] | K.I. Tserpes;P. Papanikos;G. Labeas;Sp. Pantelakis.Fatigue damage accumulation and residual strength assessment of CFRP laminates[J].Composite Structures,20042(2):219-230. |
[6] | 吴富强 .纤维增强复合材料寿命预测与疲劳性能衰减研究[D].南京航空航天大学,2008. |
[7] | W.Van Paepegem;J.Degrieck.Experimental set-up for and numerical modelling of bending fatigue experiments on plain woven glass/epoxy composites[J].Composite Structures,20011(1):1-8. |
[8] | 程光旭;韦玮;李光哲.复合材料疲劳损伤演化的两阶段模型[J].机械工程材料,2000(5):1-4. |
[9] | W. Van Paepegem;J. Degrieck.A new coupled approach of residual stiffness and strength for fatigue of fibre-reinforced composites[J].International Journal of Fatigue,20027(7):747-762. |
[10] | Alireza Shirazi;A. Varvani-Farahani.A Stiffness Degradation Based Fatigue Damage Model for FRP Composites of (0/θ) Laminate Systems[J].Applied composite materials,20102(2):137-150. |
[11] | J. Tong.Characteristics of fatigue crack growth in GFRP laminates[J].International Journal of Fatigue,20022/4(2/4):291-297. |
[12] | A.W. Wharmby;F. Ellyin;J.D. Wolodko.Observations on damage development in fibre reinforced polymer laminates under cyclic loading[J].International Journal of Fatigue,20035(5):437-446. |
[13] | 杨忠清 .玻璃纤维增强树脂基复合材料疲劳行为研究[D].南京航空航天大学,2008. |
[14] | C. -H. Lee;M. -H. R. Jen.Fatigue response and modelling of variable stress amplitude and frequency in AS-4/PEEK composite laminates, part 1:experiments[J].Journal of Composite Materials,200011(11):906-929. |
[15] | C.-H. Lee;M. -H. R. Jen.Fatigue response and modelling of variable stress amplitude and frequency in AS-4/PEEK composite laminates, part 2: analysis and formulation[J].Journal of Composite Materials,200011(11):930-953. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%