在关于拉脱载荷下Z-pin增强T型接头的有限元模拟方法基础上,通过对2组蒙皮厚度分别为7.2 mm和4.0 mm的试验件的试验结果进行分析,研究了T型接头蒙皮厚度对 Z-pin增强效果的影响。结果表明：Z-pin增强效果随着蒙皮厚度的减小而增大。蒙皮厚度大于5 mm,Z-pin不能提高结构的最大承载能力,但可显著提高结构首次掉载后的承载性能,使T型接头在较大的加载位移下仍保持较高的承载能力；无论蒙皮厚薄,结构首次掉载后,各Z-pin增强T型接头可达到的载荷平台是相当的,且该载荷平台随蒙皮的变厚有降低的趋势。
This paper is based on the finite element simulation method for Z-pin reinforced T-joints about pull-off load.After the analysis on the test results of specimens with two different skin thicknesses (7.2 mm and 4.0 mm respectively),influence of skin thickness on the reinforcing effect of Z-pin was studied.Results show that the rein-forcing effect of Z-pin increases as the thickness of skin decreases.When the skin is thicker than 5 mm,Z-pin cannot increase the maximum load-carrying capacity of structure any more,while Z-pin can still enhance the load-carrying performance after the first peak load,thus make the T-joints remain high load-carrying capacity under big load dis-placement.Whatever the thickness of skin is,load plateaus of Z-pin reinforced T-joints after first peak load are al-most the same and the level of load plateau decreases as the thickness of skin increases.
参考文献
| [1] | Ivana K. Partridge;Denis D.R. Cartie.Delamination resistant laminates by Z-Fiber~R pinning: Part I manufacture and fracture performance[J].Composites, Part A. Applied science and manufacturing,20051(1):55-64. |
| [2] | D. D. R. Cartie;G. Dell'Anno;E. Poulin.3D reinforcement of stiffener-to-skin T-joints by Z-pinning and tufting[J].Engineering Fracture Mechanics,200616(16):2532-2540. |
| [3] | Denis D.R. Cartie;Manos Troulis;Ivana K. Partridge.Delamination of Z-pinned carbon fibre reinforced laminates[J].Composites science and technology,20066(6):855-861. |
| [4] | 王鹏 .复合材料Z-pin增强技术及力学性能研究[D].南京航空航天大学,2011. |
| [5] | Yong-Bin Park;Byeong-Hee Lee;Jin-Hwe Kweon;Jin-Ho Choi;Ik-Hyeon Choi.The strength of composite bonded T-joints transversely reinforced by carbon pins[J].Composite structures,20122(2):625-634. |
| [6] | 叶强 .层合复合材料的粘聚区模型及其应用研究[D].南京航空航天大学,2012. |
| [7] | 李梦佳;陈普会;孔斌;彭涛;姚正兰;邱学仕.Z-pin参数对复合材料T型接头拉脱承载能力的影响[J].复合材料学报,2015(2):571-578. |
| [8] | Pegorin, F.;Pingkarawat, K.;Daynes, S.;Mouritz, A. P..Influence of z-pin length on the delamination fracture toughness and fatigue resistance of pinned composites[J].Composites, Part B. Engineering,2015Sep.(Sep.):298-307. |
| [9] | T.M. Koh;S. Feih;A.P. Mouritz.Strengthening mechanics of thin and thick composite T-joints reinforced with z-pins[J].Composites, Part A. Applied science and manufacturing,20128(8):1308-1317. |
| [10] | 段沐枫;李宁;郑莹莹;肖军;李勇.K-cor夹层结构制备工艺[J].宇航材料工艺,2012(5):21-25. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%