选用3种不同链长的烷基季铵盐阳离子表面活性剂即十二烷基三甲基溴化铵(DTAB)、十四烷基三甲基溴化铵(TTAB)和十六烷基三甲基溴化铵(CTAB)对粉煤灰漂珠(FAFB)进行改性,并将改性产物与苯胺(An)共混进行乳液聚合,制备聚苯胺@有机改性粉煤灰漂珠(PAn@OFAFB)复合材料.采用化学元素分析、FTIR、XRD、SEM、TGA、数字四探针测试仪、LCR数字电桥和旋转流变仪对复合材料进行结构表征以及电流变性能分析.结果表明:改性剂的碳链长度越长,改性效果越好,CTAB吸附在FAFB表面的量最多,且表面吸附率为1.91wt％,PAn和OFAFB复合程度越明显,FAFB表面包覆的PAn越多;聚苯胺@十六烷基三甲基溴化铵改性粉煤灰漂珠(PAn@FAFB-CTAB)的电导率最大为0.06 S·cm-1;将其作分散相制成的电流变液比PAn-十二烷基苯磺酸(PAn DBSA)具有更好的电流变效应,抗击穿能力较纯PAn提高了0.5 kV/mm;将FAFB作为PAn的载体能够提高复合材料的悬浮稳定性;引入FAFB-CTAB可以显著改善复合材料的热稳定性,且PAn的相对包覆量为28.07wt％.
参考文献
| [1] | 向礼琴;赵晓鹏.蒙脱土/二氧化钛复合颗粒电流变液材料的制备及其性能[J].化学学报,2003(11):1867-1871. |
| [2] | 尹剑波;赵晓鹏.石墨烯/聚合物纳米复合电流变材料[J].高分子学报,2012(12):1355-1363. |
| [3] | Hwai-Chung Wu;Peijiang Sun.New building materials from fly ash-based lightweight inorganic polymer[J].Construction and Building Materials,20071(1):211-217. |
| [4] | Sung BH;Choi US;Jang HG;Park YS.Novel approach to enhance the dispersion stability of ER fluids based on hollow polyaniline sphere particle[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,20061/3(1/3):37-42. |
| [5] | 翟冠杰;符爱云;董岩.粉煤灰漂珠纳米结构及绝热研究[J].德州学院学报,2003(2):46-48. |
| [6] | 徐风广;蒋建萍.漂珠理化性质的研究及应用[J].粉煤灰综合利用,2002(4):42-43. |
| [7] | 王悦;雷西萍;宋学锋;蔺彦梅;王冰鑫.氧化剂浓度对漂珠/聚苯胺复合材料的制备及其性能影响研究[J].硅酸盐通报,2014(12):3090-3096. |
| [8] | 蔺彦梅;雷西萍;宋学锋;王悦;王冰鑫.聚苯胺@粉煤灰漂珠复合材料的导电及介电性能[J].复合材料学报,2015(4):948-954. |
| [9] | Banerjee SS;Joshi MV;Jayaram RV.Effect of quaternary ammonium cations on dye sorption to fly ash from aqueous media[J].Journal of Colloid and Interface Science,20062(2):477-483. |
| [10] | 吴平霄;李荣;党志.不同链长季铵盐柱撑新疆蛭石的层间结构分析[J].华南理工大学学报（自然科学版）,2006(5):15-19,37. |
| [11] | Gok A;Omastova M;Prokes J.Synthesis and characterization of red mud/polyaniline composites: Electrical properties and thermal stability[J].European Polymer Journal,20076(6):2471-2480. |
| [12] | Prokes J.;Tobolkova E.;Stejskal J.;Krivka I..Enhanced stability of polyaniline/inorganic salt composites during temperature cycling[J].Polymer Degradation and Stability,20002(2):261-269. |
| [13] | Shadi Jafarzadeh;Esben Thormann;Ted Ronnevall.Toward Homogeneous Nanostructured PolyaniIine/Resin Blends[J].ACS applied materials & interfaces,20115(5):1681-1691. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%