采用布拉格光纤光栅(FBG)传感器,对一种典型液态成型环氧树脂在不同固化工艺以及后固化过程中的温度及应变进行了实时在线监测。通过将树脂内部应变变化转化为树脂线性体积变化,得到不同工艺过程中树脂的固化收缩规律,以此作为依据对树脂的经验固化及后固化工艺参数进行验证和优化。结果表明：所选液态成型树脂在80℃下固化,其固化度和玻璃化转变温度分别为90%和85℃,高于75℃固化树脂,但其总固化体积收缩只比75℃固化时略为增加了约5%；树脂在120℃下进行后固化处理时,恒温180 min后FBG传感器监测到的树脂内部应变已不再变化,此时树脂已基本完全固化,无需再延长后固化时间。
Temperature and strain in a representative liquid molding epoxy resin were in-situ monitored by Fiber Bragg Grating (FBG)sensors throughout different curing processes and post-curing processes.Curing shrinkage regularity of the resin in different processes was derived from its linear volume variation transformed from the strain evolution in resin.Process parameters of experiential curing and post-curing processes were validated and optimized based on the curing shrinkage.The results show that conversion degree and glass transition temperature of the liquid moldingresin cured at 80 ℃ are 90% and 85 ℃ respectively,which are higher than resin cured at 75 ℃.However, total curing shrinkage of the resin cured at 80 ℃ is only 5% higher than cured at 75 ℃.The strain in resin becomes constant after 180 min in isothermal procedure of 120 ℃ post-curing,which means the resin is cured completely. There is no need to extend the post-curing time.
参考文献
| [1] | 寇哲君;戴棣;曹正华.复合材料结构固化变形预测[J].材料工程,2007(z1):225-228. |
| [2] | 程文礼;邱启艳;陈静.热压罐成型复合材料固化变形机理及控制研究[J].材料导报,2012(z1):410-414. |
| [3] | M.R. Wisnom;M. Gigliotti;N. Ersoy.Mechanisms generating residual stresses and distortion during manufacture of polymer-matrix composite structures[J].Composites, Part A. Applied science and manufacturing,20064(4):522-529. |
| [4] | Lolei Khoun;Pascal Hubert.Investigation of the dimensional stability of carbon epoxy cylinders manufactured by resin transfer moulding *[J].Composites, Part A. Applied science and manufacturing,20101(1):116-124. |
| [5] | Tomasz Garstka;N. Ersoy;K.D. Potter.In situ measurements of through-the-thickness strains during processing of AS4/8552 composite[J].Composites, Part A. Applied science and manufacturing,200712(12):2517-2526. |
| [6] | Nuri Ersoy;Tomasz Garstka;Kevin Potter.Development of the properties of a carbon fibre reinforced thermosetting composite through cure[J].Composites, Part A. Applied science and manufacturing,20103(3):401-409. |
| [7] | Chun Li;Kevin Potter;Michael R. Wisnom.In-situ measurement of chemical shrinkage of MY750 epoxy resin by a novel gravimetric method[J].Composites science and technology,20041(1):55-64. |
| [8] | Patricia P. Parlevliet;Harald E.N. Bersee;Adriaan Beukers.Shrinkage determination of a reactive polymer with volumetric dilatometry[J].Polymer Testing,20104(4):433-439. |
| [9] | Jung WK;Chu WS;Ahn SH;Won MS.Measurement and compensation of spring-back of a hybrid composite beam[J].Journal of Composite Materials,20077(7):851-864. |
| [10] | Patricia Prasatya;Gregory B.McKenna;Sindee L.Simon.A Viscoelastic Model for Predicting Isotropic Residual Stresses in Thermosetting Materials: Effects of Processing Parameters[J].Journal of Composite Materials,200110(10):826-848. |
| [11] | J.M. Svanberg;J.A. Holmberg.An experimental investigation on mechanisms for manufacturing induced shape distortions in homogeneous and balanced laminates[J].Composites, Part A. Applied science and manufacturing,20016(6):827-838. |
| [12] | Parlevliet, PP;Bersee, HEN;Beukers, A.Measurement of (post-)curing strain development with fibre Bragg gratings[J].Polymer Testing,20103(3):291-301. |
| [13] | 秦伟;吴晓宏;曹茂盛.RTM工艺成型复合材料树脂固化过程残余应变监测研究[J].航空材料学报,2005(4):50-52. |
| [14] | 陈宏伟;李炜.Bragg光栅传感器在复合材料加工与检测中的应用[J].纤维复合材料,2009(3):26-28. |
| [15] | 李雪芹;周玉敬;张子龙;刘刚;益小苏.光纤布拉格光栅传感器监测环氧树脂固化收缩研究[J].材料工程,2012(8):73-77. |
| [16] | 甘丽;孙志杰;顾轶卓;李敏;张佐光.升温与等温法非模型动力学研究环氧树脂固化反应[J].高分子学报,2010(8):1016-1022. |
| [17] | 吴唯;刘明昌;陈玉;浦伟光;吴祥.E-51环氧树脂固化反应中动力学转变[J].复合材料学报,2011(4):1-6. |
| [18] | 李恒;王德海;钱夏庆.环氧树脂固化动力学的研究及应用[J].玻璃钢/复合材料,2013(4):43-50. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%