利用材料试验机和分离式霍普金森压杆(SHPB)系统对加压烧结制备的Zr-W多功能含能结构材料在不同应变率下的压缩行为进行测试。通过在试样上直接贴应变片与波形整形技术相结合，实现了恒应变率动态加载。试验结果表明：该材料在准静态和动态加载下均呈现良好的线弹性，弹性模量对应变率效应不敏感，约为186 GPa。烧结生成的W2 Zr相显著提高了Zr-W材料的强度和脆性，试样在强冲击载荷作用下发生破碎反应并释放大量的热量，表现出很高的含能特性，动态破坏应变和破坏强度表现出一定的正应变率效应。
The compressive behavior of pressing sintering Zr-W multifunctional energetic structural material was tested at different strain rates by using material testing machine and split Hopkinson pressure bar (SHPB)system. A constant strain rate dynamic loading can be obtained by combination of attaching a strain gauge directly to the sample and employing the pulse shaping technique.Test results show that Zr-W material appears good linear elastic-ity both under quasi-static and dynamic loading,and its elastic modulus is about 186 GPa,not so sensitive to stain rate effect.The Zr-W material presents high-strength and brittle which is attributed to the W2 Zr sintering product phase,and it can fragment,react and rapidly release high amounts of energy under strong impacting load.The re-sults show that the Zr-W material has high energy,and its dynamic failure strain and failure strength increase with the strain rate increasing.
参考文献
| [1] | 张先锋;赵晓宁.多功能含能结构材料研究进展[J].含能材料,2009(6):731-739. |
| [2] | 王树山;李朝君;马晓飞;隋树元.钨合金破片对屏蔽装药撞击起爆的实验研究[J].兵工学报,2001(2):189-191. |
| [3] | 陈伟;赵文天;王健;梁栋;葛文艳;熊晓松.钨锆合金破片毁伤过程研究[J].兵器材料科学与工程,2009(2):108-111. |
| [4] | 张将;张先锋;范秉源;何勇;顾晓辉.钨锆合金的动态力学特性研究[J].兵器材料科学与工程,2013(1):3-6. |
| [5] | X. F. Zhang;A. S. Shi;L. Qiao;J. Zhang;Y. G. Zhang;Z. W. Guan.Experimental study on impact-initiated characters of multifunctional energetic structural materials[J].Journal of Applied Physics,20138(8):083508-1-083508-10. |
| [6] | ANDREW COVERDILL;CHRISTOPHER DELANEY;ANDREW JENNRICH.Tungsten Combustion in Explosively Initiated W/Zr Mechanical Alloys[J].Journal of Energetic Materials,20143(3):135-145. |
| [7] | 罗骥;曹慧钦;贾步超;杨薇薇;陈存广.新型铜基受电弓滑板材料的制备与性能[J].复合材料学报,2012(2):103-108. |
| [8] | Frew DJ.;Forrestal MJ.;Chen W..Pulse shaping techniques for testing brittle materials with a split Hopkinson pressure bar[J].Experimental Mechanics,20021(1):93-106. |
| [9] | Frew DJ.;Chen W.;Forrestal MJ..A split Hopkinson pressure bar technique to determine compressive stress-strain data for rock materials[J].Experimental Mechanics,20011(1):40-46. |
| [10] | 任会兰;龙波;宁建国;褚亮.ZrO2增韧Al2O3陶瓷的力学性能和增韧机制[J].复合材料学报,2015(3):776-781. |
| [11] | 宁建国;任会兰;方敏杰.基于椭圆形微裂纹演化与汇合的准脆性材料本构模型[J].科学通报,2012(21):1978-1986. |
| [12] | Pan Y;Chen W;Song B.Upper limit of constant strain rates in a split Hopkinson pressure bar experiment with elastic specimens[J].Experimental Mechanics,20055(5):440-446. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%