借助ANSYS/LS-DYNA软件，建立楔横轧层合轴有限元模型，根据四因素三水平的正交实验进行部分厚径比轧制实验。通过有限元数值模拟，分析工艺参数成形角、展宽角、断面收缩率和轧制温度对厚径比的影响规律。结果表明：轧制实验结果和有限元模拟的结果相符合，有限元模型可以用来预测厚径比。厚径比随着展宽角的增大先迅速下降，后缓慢下降；随着轧制温度的增大先增加，后缓慢增加；随着断面收缩率的增大先缓慢增加，后趋于平缓；随着成形角的增大变化不明显。对厚径比的影响主次为：展宽角、轧制温度、断面收缩率、成形角。研究结果有助于指导层合轴覆材厚度和基材半径尺寸的调控与设计。
By using ANSYS/LS-DYNA software,the finite element(FE)model of cross-wedge rolling of laminated shafts was established.Some thickness-radius ratio rolling experiments were carried out under the orthogonal exper-imental designed with four factors and three levels.Through finite element simulation,the effect of process parame-ters including forming angle,spreading angle,area reduction and rolling temperature on thickness-radius ratio were analyzed.The results show that the rolling experimental results accord with the simulation results,which shows that finite element model can be used to predict thickness-radius ratio.With the increase of spreading angle,the thickness-radius ratio sharply decreases first and then slowly decreases.With the increase of temperature,the thick-ness-radius ratio strengthens first and then slowly strengthens.With the increase of area reduction,the thickness-radius ratio slowly strengthens first and then changes little.With the increase of forming angle,the thickness-radius ratio change is not obvious.The influencing sequence on the thickness-radius ratio is spreading angle,rolling tem-perature,area reduction and forming angle in turn.The research results contribute to control and design clad materi-al thickness and matrix material radius size of laminated shaft.
参考文献
| [1] | 杨合;李落星;王渠东;郭良刚.轻合金成形领域科学技术发展研究[J].机械工程学报,2010(12):31-42. |
| [2] | 杨勇;何涛;汪泽轩;李燕;王涛.T91楔横轧成形过程的数值模拟与分析[J].锻压技术,2015(10):148-153. |
| [3] | PATER Zbigniew;GONTARZ Andrzej;TOFIL Arkadiusz.Analysis of the Cross-Wedge Rolling Process of Toothed Shafts Made from 2618 Aluminium Alloy[J].上海交通大学学报(英文版),2011(2):162-166. |
| [4] | 霍元明;王宝雨;林建国;周靖.楔横轧高铁车轴钢25CrMo4塑性损伤形成机理[J].东北大学学报（自然科学版）,2013(11):1625-1629. |
| [5] | 郑振华;刘晋平;王宝雨;胡正寰.成形角对楔横轧21-4N合金钢气门心部质量的影响[J].北京科技大学学报,2013(2):228-233. |
| [6] | 黄江华;刘晋平;王宝雨;胡正寰.4Cr9Si2马氏体钢气门楔横轧工艺研究[J].中南大学学报（自然科学版）,2013(7):2744-2750. |
| [7] | 张宁;王宝雨;胡正寰.楔横轧成形GH4169合金的热力耦合数值模拟[J].北京科技大学学报,2011(11):1396-1401. |
| [8] | 刘文萍;彭文飞;束学道;孙宝寿.楔横轧同种材料层合轴的展宽段应力分析[J].塑性工程学报,2014(5):82-87. |
| [9] | 张建华;彭文飞;沈法;束学道;刘文萍.基于应力应变的楔横轧层合轴分界面结合机理研究[J].热加工工艺,2015(17):80-83. |
| [10] | 蔺永诚;陈明松;钟掘.42CrMo钢的热压缩流变应力行为[J].中南大学学报（自然科学版）,2008(3):549-553. |
| [11] | 孙影;张麦仓;董建新;杨忠民.Q235钢的热变形特性[J].钢铁研究学报,2006(5):42-45,59. |
| [12] | 李传民;束学道;胡正寰.楔横轧多楔轧制铁路车轴可行性有限元分析[J].中国机械工程,2006(19):2017-2019. |
| [13] | 束学道;彭文飞;聂广占;胡正寰.楔横轧大型轴类件轧制力规律研究[J].塑性工程学报,2009(1):102-105,114. |
| [14] | 彭文飞;焦思佳;束学道;张康生.楔横轧非对称轴类件的可行性分析[J].中南大学学报（自然科学版）,2012(11):4280-4285. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%