分别用电子束焊(EBW)及钨极氩弧焊(GTA)两种焊接方法对Fe-Al基合金试样进行了焊接性研究.结果表明,用EBW方法可以成功地得到无裂纹与缺陷的Fe-Al基合金焊缝;对GTA方法,需采用预热及焊后缓冷工艺方可有效地阻止延迟冷裂纹的产生,选择中低碳CrMo钢焊丝作填充材料,使Fe3Al基合金具有较好的焊接性.同种材料,同种焊丝,在保证焊透的情况下,减小焊接电流和热输入,有利于提高材料的抗裂能力.
参考文献
| [1] | McKamey C G, Devan J H, Tortorelli P F, Sikka V K. J Mater Res, 1991; 6:1779 |
| [2] | Sun Z Q, Huang Y D, Yang W Y, Chen G L. Mater Res Soc Symp Proc, 1993; 288:885 |
| [3] | David S A, Zacharia T. Weld J, 1993; 72(5): 201-s |
| [4] | Goodwin G M, McKamey C G, Maziasz P J, Sikka V K.DE90012722/XAD, Report of The US Department of Energy, Oak Ridge National Laboratory, 1990:181 |
| [5] | Dong M. Master Thesis, University of Science and Technology Beijing, 1999(董敏.北京科技大学硕士学位论文,1999) |
| [6] | Santella M L, David S A. Weld J, 1986; 65(5): 129-s |
| [7] | Liu Y D. Master Thesis, University of Science and Technology Beijing, 1997(刘豫东.北京科技大学硕士学位论文,1997) |
| [8] | Liu C T, McKamey C G, Lee E H. Scr Metall Mater, 1990;24:385 |
| [9] | Stoloff N S, Liu C T. Intermetallic, 1994; 2:2033 |
| [10] | Goodwin G M. DE94001091, Report of The US Department of Energy, Oak Ridge National Laboratory, 1994 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%