利用Ti与B之间的自蔓延高温合成反应,经非自耗电弧熔炼工艺制备了TiB增强的钛基复合材料.借助X射线衍射(XRD)、扫描电镜和透射电镜分析了复合材料的物相和增强体的形态.结果表明:只存在TiB增强体和α-Ti.原位合成增强体TiB的形貌与其B27晶体结构密切相关,TiB增强体容易沿[010]方向生长而长成柱状短纤维.其柱面由(100),(101)和(101)组成.
参考文献
| [1] | Ranganath S. J Mater Sci, 1997; 32:1 |
| [2] | Zhang X N, Lii W J, Zhang D, Wu R J, Bian Y J, Fang P W. Aerosp Mater Technol, 1998; 28(2): 24(张小农,吕维洁,张荻,吴人洁,卞玉君,方平伟.宇航材料工艺,1998;28(2):24) |
| [3] | Jiang J Q, Lim T S, Kim Y J, Kim B K, Chung H S. Mater Sci Technol, 1996; 12:362 |
| [4] | Fan Z, Niu H J, Miodownik A P, Saito T, Cantor B. Key Eng Mater, 1997; 127-131:423 |
| [5] | Tsang H T, Chao C G, Ma C Y. Scr Mater, 1997; 37:1359 |
| [6] | Dubey S, Lederich R, Soboyejo W. Metall Mater Trans, 1997;28A: 2037 |
| [7] | Takahashi T. J Jpn Inst Met, 1995; 59:244(高桥辉南.日本金属学会志,1995;59:244) |
| [8] | Lü W J, Zhang X N, Zhang D, Wu R J, Bian Y J, Fang P W. Acta Metall Sin, 1999; 35:536(吕维洁,张小农,张荻,吴人洁,卞玉君,方平伟.金属学报,1999;35:536) |
| [9] | Knacke O, Kubaschewski O, Hesselmann K. Thermochemical Properties of Inorganic Substances. 2nd ed, New York:Springer-Verlag, 1991: 115, 2057, 2108 |
| [10] | Merzhanov A G. Combust Sci Technol, 1975; 10(1): 195 |
| [11] | Duschanek H, Rogl P, Lukas H L. J Phase Equilib, 1995; 16:46 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%