采用溶胶-凝胶氧化铝涂覆硼酸铝晶须方法改善挤压铸造晶须增强6061Al复合材料的界面性能.对复合材料的界面观察表明,γ-Al2O3和α-Al2O3涂层均可抑制尖晶石界面反应,而且涂层较厚时涂层效果明显.界面反应程度的差异也影响复合材料的弯曲性能和时效行为.界面反应越轻微,则复合材料的弹性模量越大、峰时效过程由于基体中Mg的较少消耗而推迟.涂层复合材料的弯曲断裂以晶须拔出为主,而无涂层复合材料的弯曲断裂以近界面基体断裂为主.与γ-Al2O3涂层相比,α-Al2O3涂层的界面改性作用更显著.
参考文献
| [1] | Nair S V. Int Mater Rev, 1985; 30:275 |
| [2] | Rabiei A, Kim B N, Enoki M, Kishi T. Trans JIM, 1996; 37:1148 |
| [3] | Wang D Z, Peng H X. Wear, 1995; 184:187 |
| [4] | Pan J, Ning X G, Hu K Y, Ye H Q. Acta Metall Sin, 1993;29:B280(潘进,宁小光,胡魁毅,叶恒强.金属学报,1993;29:B280) |
| [5] | Ning X G, Pan J, Li J H, Hu K Y, Ye H Q, Fukunaga H. J Mater Sci Lett, 1993; 12:1644 |
| [6] | Suganuma K, Sasaki G, Fujita T, Suzuki N. J Jpn Inst Light Met Soc, 1991; 41:297(菅沼克昭,佐佐木元,藤田辉昭,铃木信幸.轻金属,1991;41:297) |
| [7] | Nagatomo K, Suganuma K. J Jpn Inst Met, 1994; 58:78(永友贤治,菅沼克昭.日本金属学会志,1994;58:78) |
| [8] | Nukami T, Shintani Y, Suganuma T. Toyota Tech Rev, 1993;43:62(额见哲也,新谷良智,菅沼徹哉.トョ夕自动车,1993;43:62) |
| [9] | Lee B I, Park S Y. J Am Ceram Soc, 1989; 72:238 |
| [10] | Fei W D, Jiang X D, Li C, Yao C K. J Mater Sci Lett, 1996;15:1966 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%