在高温气相反应器中,利用掺AlCl3的TiCl4氧化反应制备金红石型纳米TiO2颗粒.研究了氧气预热温度、反应器尾部氮气流量、反应温度、停留时间等对TiO2颗粒大小的影响.结果表明:提高氧气预热温度和加大反应器尾部氮气流量对控制产物粒径有利,TiO2粒径随反应温度升高和停留时间延长而增大.当反应温度为1373 K,AlCb与TiCl4摩尔比为0.25、停留时间为1.73 s时,纯金红石相纳米TiO2颗粒的粒径分布为30-50 nm.
参考文献
| [1] | Li Y N. Hydrometallurgy, 1995; 2:25(李雁南湿法冶金,1995;2:25) |
| [2] | Tang Y Q, Zhou X W. Mater Rev, 1995; 9:20(唐阳清,周馨我.材料导报,1995;9:20) |
| [3] | Chen D R, Meng Y D, Fang Y P. Chin J Inorg Chem, 1995;11:228(陈代荣,孟永德,樊悦朋无机化学学报,1995;11:228) |
| [4] | Ivanda G M, Sekulie A, Music S, Popovic S, Turkovic A,Furic K. Mater Lett, 1996; 28:225 |
| [5] | Shi L Y, Hua B, Zhang J P. Functional Mater, 1998; 29:136(施利毅,华彬,张剑平.功能材料,1998;29:136) |
| [6] | Shi L Y, Li C Z, Fang D Y. Mater Rev, 1998; 12:23(施利毅,李春忠,房鼎业材料导报,1998;12:23) |
| [7] | Prastinis S E, Vemury S. Powder Technol, 1996; 88:267 |
| [8] | Vemury S, Pratsinis S E. J Am Ceram Soc, 1995; 78:2984 |
| [9] | Li H R, Chen H S, Yang X H. Practical Coordinating Titration. Guangzhou: Zhongshan University Press, 1987:227(李焕然,陈焕生,杨秀环.实用络合滴定.广州:中山大学出版社.1987:227) |
| [10] | Prastinis S E, Bai H, Biswas P. J Am Ceram Soc, 1990; 73:2158 |
| [11] | Yu J G. Chem Bulletin, 1991; 10:25(余家国化学通报,1991,10:25) |
| [12] | Dennis R ed; Liang H F, LU D Z trans. Handbook of Aerosol.Beijing: Atomic Energy Press, 1988:162(Dennis R著,梁鸿富,卢定正译.气溶胶手册.北京:原子能出版社,1988:162) |
| [13] | Shi L Y, Chen A P, Zhu Y H, Li C Z, Fang D Y. Chem React Eng Technol, 1999; 15:213(施利毅,陈爱平,朱以华,李春忠,房鼎业.化学反应工程与工艺,1999;15:213 |
| [14] | Shi L Y. Ph.D. thesis, East China University of Science and Technology, 1999:67(施利毅.上海:华东理工大学博士学位论文,1999:67) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%