利用磁控溅射技术制备了Fe含量(质量分数,%)分别为25和50的两种Fe-Cu纳米涂层,并研究了该涂层在700与800℃空气中的氧化.结果表明,Fe-75Cu涂层氧化后形成了外层为氧化铜和内侧为氧化铁的复合氧化膜,而Fe-50Cu发生了Ee的单一外氧化,其氧化特征均有别于同成分的铸态合金.这种氧化机制在于晶粒尺寸细化显著扩展了Fe在Cu中的溶解度,同时大量的晶界也为组元扩散提供了短路通道,晶粒尺寸纳米化有助于降低难互溶双相合金体系中发生最活泼组元由内氧化向单一外氧化转变的临界浓度.
参考文献
| [1] | Gesmundo F, Niu Y, Oquab D, Roos C, Pieraggi B, Viani F. Oxid Met, 1998; 49:115 |
| [2] | Niu Y, Li Y S, Gesmundo F. Corros Sci, 2000; 42:165 |
| [3] | Niu Y, Li Y S, Gesmundo F,Viani F. Intermetallics, 2000;8:293 |
| [4] | Li Y S, Niu Y, Gesmundo F. High Temp Mater Proc, 1999;18:185 |
| [5] | Fu G Y, Guan H R, Niu Y, Li Y S, Zhao Z L, Wu W T.Acta Metall Sin, 2000; 36:279(傅广艳,管恒荣,牛焱,李远士,赵泽良,吴维 .金属学报,2000;36:279) |
| [6] | Li Y S,Niu Y,Wang F G,Song J X,Wu W T.Acta Metall Sin.1999;35:1171(李远士,牛焱,王富岗,宋尽霞,吴维 .金属学报,1999;35:1171) |
| [7] | Wang F H, Young D J. Oxid Met, 1997; 48:497 |
| [8] | Wang F H. Oxid Met, 1997; 48:215 |
| [9] | Gesmundo F, Viani F, Niu Y. Oxid Met, 1996; 45:51 |
| [10] | Niu Y. Gesmundo F, Viani F, Wu W T. Oxid Met, 1996;46:525 |
| [11] | Jiang J Z, Gente C, Bormann R. Mater Sci Eng, 1998;A242:268 |
| [12] | Qi M, Zhu M, Yang D Z. J Mater Sci Lett, 1994; 13:966 |
| [13] | Yang Y Z, Ma X M, Dong Y D. Acta Metall Sin, 1992;A28:399(杨元政,马学鸣,董远达.金属学报,1992;A28:399) |
| [14] | Wu Y K,Huang J Y,He A Q,Hu K Y,Meng X M.Acta Metall Sin,1993;B29:545(吴玉琨,黄建宇,何安强,胡魁毅,孟祥敏.金属学报,1993;B29:545) |
| [15] | Sui H X,Zhu M,Qi M,Li G B,Yang D Z.J Appl Phys Lett,1992;71:2945 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%