研究了磁控溅射NiAl微晶涂层对NiAl-TiC(20%,体积分数)复合材料1000-1100℃高温氧化性能的影响.结果表明,NiAl微晶涂层大大提高了NiAl-TiC复合材料的恒温及循环氧化性能,降低氧化速率几个数量级,对于NiAl-TiC复合材料来说,其表面形成以TiO2为主的复合氧化物,而施加NiAl微晶涂层后,其表面氧化物主要是Al2O3.
参考文献
| [1] | Miracle D B. Acta Metall Mater, 1993; 41:649 |
| [2] | Vedula K, Pathave V, Aslanidis I, TiTran R H. Mat Res Soc Symp Proc, 1985; 39:411 |
| [3] | Vedula K, Stephens J R. Mat Res Soc Syrnp Proc, 1987;81:381 |
| [4] | Kumar K S, Whittenberger J D. Mater Sci Technol, 1992;8:317 |
| [5] | Whittenberger J D, Viswanadham R K, Mannan S K,Sprissler B. J Mater Sci, 1990; 25:35 |
| [6] | Wang L, Arsenault R J. Mater Sci Eng, 1990; A127:91 |
| [7] | Whittenberger J D, Kumar K S, Mannan S K. Mater High Temp, 1991; 9:3 |
| [8] | Alman D E, Stoloff N S. Int J Powder Metall, 1991; 27:29 |
| [9] | Xing Z P, Dai J Y, Guo J T, An G Y, Hu Z Q. Scripta Metall Mater, 1994; 31:1141 |
| [10] | Xing Z P, Yu L G, Guo J T, J, Dai Y, An G Y, Hu Z Q. J Mater Sci Lett, 1995; 14:443 |
| [11] | Baker I, Munroe P R. J Met, 1988; 40:28 |
| [12] | Xing Z P, Guo J T, Han Y F, Yu L G. Metall Mater Trans,1997; 28A: 1079 |
| [13] | Guo J T, Xing Z P, Wang S H, Li H. JIron Steel Res,1997; 9:23(郭建亭,邢占平,王淑荷,李辉.钢铁研究学报增刊,1997;9:23) |
| [14] | Xing Z P, Guo J T, Hu Z Q, An G Y. Acta Metall Sin,1994; 7:45 |
| [15] | Xing Z P, Yu L G, GuoJT, Dai J Y, AnGY, Hu Z Q.'J Mater Sci Lett, 1995; 14:443 |
| [16] | Jiang D T. Doctoral Thesis, Institute of Metal Research,The Chinese Academy of Sciences, Shenyang, 1998:12(姜东涛.博士学位论文,中国科学院金属研究所,沈阳,1998:12) |
| [17] | Tang Z L, Wang F H, Wu W T. Oxid Met, 1997; 48:511 |
| [18] | Yang S L, Wang F H. Acta Metall Sin, 2000; 36:511(杨松岚,王福会.金属学报,2000;36:511) |
| [19] | Gesmundo F, Viani F, Niu Y, Douglass D L. Oxid Met,1994; 39:197 |
| [20] | Gesmundo F, Viani F, Niu Y. Oxid Met, 1994; 42:285 |
| [21] | Gesmundo F, Viani F, Niu Y, Douglass D L. Oxid Met,1994; 42:409 |
| [22] | Gesmundo F, Viani F, Niu Y. Oxid Met, 1994; 42:465 |
| [23] | Niu Y, Gesmundo F, Viani F, Wu W T. Oxid Met, 1997;47:21 |
| [24] | Rahmal A, Spencer P J. Oxid Met, 1991; 35:53 |
| [25] | Backer S, Rahmel A, Schorr M, Schitze M. Oxid Met,1992; 38:425 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%