利用选区电子衍射和会聚束衍射研究了喷射沉积Al-Fe-V-Si合金中一种六方相的晶体结构,其点阵常数为:a=2.52 nm,c=1.26 nm,空间群为P6/mmm.该六方相与立方相具有固定取向关系,且EDS分析表明,两相成分相近.系统对比分析SAED花样发现,六方相的某些带轴衍射谱具有立方相的二十面体结构基元表现出的衍射特征,表明六方相也是一种准晶近似晶体相,其结构构架可能由(Fe+V)和(Al+Si)双层二十面体结构基元以3种不同取向堆砌而成.
参考文献
| [1] | Schechtman D, Blech I, Gratias D, Cahn J W. Phys Rev Lett, 1984; 53:1951 |
| [2] | Kuo K H, Ye H Q, Li D X. J Mater Sci, 1986; 21:2597 |
| [3] | Shoemaker D P, Shoemaker C B. Mater Sci Forum, 1987;22-24:67 |
| [4] | Kreiner G, Franzen H F. J Alloy Compd, 1995; 221:67 |
| [5] | Li X Z, Hirago K, Yamamoto A. Philos Mag, 1997; A76:657 |
| [6] | Elser V, Henley L. Phys Rev Lett, 1985; 55:2883 |
| [7] | Guyot P, Audier M. Philos Mag, 1985; B52:L15 |
| [8] | Audier M and Guyot P. Philos Mag, 1986; B53:L43 |
| [9] | Koh H J, Park W J, Kim N J. Mater Trans JIM, 1998;39:982 |
| [10] | Bendersky L. J Microsc, 1987; 146:303 |
| [11] | Yang Q B, Kuo K H. Philos Mag, 1986; B53:L115 |
| [12] | Steeds J W, Vincent R. J Appl Crystallogr, 1983; 16:317 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%