利用亚点阵的准亚规则溶体模型计算了Ti-Al-Nb三元系合金热力学活度,根据金属氧化反应用热力学计算了相应的Ti/TiO和Al/Al2O3的氧平衡分压讨论了Nb合金化对γ-TiAl金属间化合物热力学活度和氧化反应的氧平衡分压的影响,计算的热力学活度与Knudsen池隙透法测量的规律相符.由Nb合金化γ-TiAl的热力学活度以及氧化反应的氧平衡分压变化不能判定Ti-Al-Nb三元系合金生成氧化物的种类及其稳定性单纯的热力学因素不足以解释Nb合金化改善γ-TiAl抗高温氧化性能的机理.
参考文献
| [1] | Becker S, Rahmel A, Schorr M, Schutze M. Oxid Met,1992,38:425 |
| [2] | Shida Y, Anada H. Corros Sci, 1993,35:945 |
| [3] | Lei M K, Zhu X P, Tang Z, Wang F. J Mater Sci Lett,2000,19:1839 |
| [4] | Stroosnijder M F, Zheng N, Quadakkers W J, Hofman R, Gil A, Lanza F. Oxid Met, 1996,46:19 |
| [5] | Luthra K L. Oxid Met, 1991,36:475 |
| [6] | Rahmel A, Spencer P J. Oxid Met, 1991,35:53 |
| [7] | Eckert M, Bencze L, Kath D, Nickel H, Hilpert K. Ber Bunsenges Phys Chem, 1996,100:418 |
| [8] | Kattner U R, Lin J C, Chang Y A. Metall Trans, 1992,23A: 2081 |
| [9] | Kattner U R, Boettinger W J. Mater Sci Eng, 1992,152A:9 |
| [10] | Zhang F, Chen S L, Chang Y A, Kattner U R. Intermetallics, 1997,5:471 |
| [11] | Ohnuma I, Fujita Y, Mitsui H, Ishikawa K, Kainuma R, Ishida K. Acta Mater, 2000,48:3113 |
| [12] | Li J T. Ph D. Thesis, Northeastern University, Shenyang,1997:103(李俊涛.东北大学博士学位论文,沈阳,1997:103) |
| [13] | Eckert M, Kath D, Hilpert K. Metal Mater Trans, 1999,30A: 1315 |
| [14] | Dinsdale A T. CALPHAD, 1991,15:317 |
| [15] | Eckert M, Hilpert K. Mater Corros, 1997,48:10 |
| [16] | Jacobson N S, Brady M P, Mehrotra G M. Oxid Met, 1999,52:537 |
| [17] | Hao Y L, Xu D S, CuiY Y, Yang R, Li D. Acta Mater,1999,47:1129 |
| [18] | Lei M K, Zhu X P, Han S Q, Wang D Y, Wang F G, Wang F. Mater Chem Phys, 2000,65:249 |
| [19] | Schmitz-Niederau M, Schutze M. Oxid Met, 1999,52:225 |
| [20] | Nickel H, Zheng N, Elschner A, Quadakkers W J. Microchim Acta, 1995,119:23 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%