研究了体积分数为15%和28%SiCw/6061Al基复合材料的同相和反相热机械疲劳寿命和损伤机制.结果表明:在小应变范围时,同相比反相疲劳寿命长,而在大应变时,同相疲劳寿命接近(对于28%SiCw)、甚至短于(对于15%SiCw)反相热机械疲劳寿命;15%SiCw/6016Al基复合材料的反相热机械疲劳寿命高于28%SiCw/6016Al基复合材料的寿命.两种材料的同相热机械疲劳寿命曲线存在交叉点,寿命高低取决于应变水平;同相和反相热机械疲劳的损伤均为空洞在SiC晶须周围基体中形核、长大和连接.
参考文献
| [1] | Qian L H,Wang Z G,Toda H,Kobyashi T.Acta Metall Sin,2001;37:1198(钱立和,王中光,户田裕之,小林俊郎.金属学报,2001;37:1198) |
| [2] | Neu R W,Sehitoglu H.Metall Trans,1989;20A:1755 |
| [3] | Mall S,Schubbe J J.Com Sci Technol,1994;50:49 |
| [4] | Zauter R,Petry F,Christ H J,Mughrabi H.In:Sehitoglu H ed,Thermo-mechanical Fatigue Behavior of Materials,Philadephia:American Society for Testing and Materials ASTM STP 1186,1993:70 |
| [5] | Liu P L,Wang Z G.Mater Sci Technol,1997;13:667 |
| [6] | Raj R.Acta Metall,1978;26:995 |
| [7] | Liu P L.Ph.D Thesis,Institute of Metal Research,The Chinese Academy of Sciences,April,1997(刘丕林,中国科学院金属研究所博士学位论文,1997) |
| [8] | Nutt S R,Duva J M.Scr Metall,1986;20:1055 |
| [9] | Christman T,Needleman A,Nutt S,Suresh S.Mater Sci Eng,1989;107A:49 |
| [10] | Wang L,Sun Z M.Kobayashi T.Scr Metall,1996;35:973 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%