制备了一种具有较宽过冷液态温度范围(△T=17 K)的非晶态Al85Ni5Y8Co2(原子分数)合金.利用差热分析、电阻测量及高分辨电镜监测了合金晶化动力学过程.结果表明,在非晶态铝合金的退火过程中纳米Al粒子的形核与长大过程是可分离的,即首先发生淬态Al晶核的长大,之后在过冷液态温区发生高密度纳米Al粒子的形核,最终是Al晶核的长大过程.
参考文献
| [1] | Inoue A. Prog Mater Sci, 1998; 43:365 |
| [2] | Greer A L. Nature, 1993; 366:303 |
| [3] | Gangopadhyay A K, Croat T K, Kelton K F. Acta Mater,2000; 48:4035 |
| [4] | Calin M, Kǒster U. Mater Sci Forum, 1998; 269-272:749 |
| [5] | Foley J C, Allen D R, Perepezko J H. Scr Mater, 1996;35:555 |
| [6] | Allen D R, Foley J C, Perepezko J H. Acta Mater, 1998;46:431 |
| [7] | Kwong V, Koo Y C, Thorpe S J, Aust K T. Acta Metall Mater, 1991; 39:1563 |
| [8] | Wang Y P, Lu K. Sci Chin, 2000; 30E: 193(王亚平, 卢柯. 中国科学, 2000; 30E: 193) |
| [9] | Perepezko J H, Wilde G. J Non-Cryst Solids, 2000; 274:271 |
| [10] | Tjong S C, Wang J Q. Z Metallkd, 2001; 92:610 |
| [11] | Chen L C, Spaepen F. Nature, 1988; 336:366 |
| [12] | Chen L C, Spaepen F. J Appl Phys, 1991; 69:679 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%