利用原子力显微镜和掠入射X射线散射技术研究了6061Al合金等离子体离子注氮表面的粗糙度和标度行为.研究结果指出,注氮初期,表面粗糙度逐渐下降;当离子注入时间较长时,表面粗糙度随注入时间的延长而逐渐增加;在远离平衡的条件下,材料的形成机制可通过分形理论进行研究.长时间离子注氮表面具有明显的分形特征,利用所得到的静态标度指数、生长指数和动态标度指数讨论了6061 Al合金离子注氮表面的标度行为.
参考文献
| [1] | Malaczynski G W, Leung C H, Elmoursi A, Hamdi A H,Campbell A B, Balogh M P, Militello M C, Simko S J,Waldo R A. Mater Sci Eng, 1999; 262:289 |
| [2] | Tendys J, Donnelly I J, Kenny M J, Pollock J T A. Appl Phys Lett, 1988; 53:2143 |
| [3] | Zhan Z, Ma X, Feng L, Sun Y, Xia L. Wear, 1998; 220:161 |
| [4] | Ma E, Liu B X, Chen X, Li H D. Thin Solid Film, 1987;147:49 |
| [5] | Family F. Physica A, 1990; 168:561 |
| [6] | Dharmadhikari C V, Ali A O, Suresh N, Phase D M,Chaudhari S M, Gane V, Gupta A, Dasannacharya B A.Solid State Comm, 2000; 114:377 |
| [7] | Li W L, Fei W D, Sun Y. Surf Coat Technol(in press) |
| [8] | Meaken P. Fractal, Scaling and Growth far from Equilibrium, Chapter. 3, Cambridge University Press, 1998 |
| [9] | Ernst H J, Folkerts R F, Lapujoulade J. Phys Rev Lett,1994; 72:112 |
| [10] | Park H, Ha M, Kim M. Phy Rev E, 1995; E51:1047 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%