固相反应法制备了Sr1-xCaxRuO3系列,X射线衍射确定样品的相结构为正交畸变钙钛矿结构.随Ca替代量x的增加,晶格常数α基本保持不变,而b和c随之减小,晶格畸变更加明显.物理性质测量系统(PPMS)测量了样品的交流磁化率,零场冷却和加场冷却磁化强度.Curie-Weiss定律确定了样品的顺磁Curie温度TP.结果表明,随x的增加,TP减小当x≤0.6时Tp大于零;当χ＞0.6时Tp小于零.利用交流磁化率随温度变化的关系确定样品的铁磁Curie温度TC,随χ的增加TC减小.当x=0.8时,TC降至4 K;而当x=1.0时,即使温度降到1.7 K,也未出现磁有序.样品磁性随Ca替代量x的变化是其结构变化的直接结果.
参考文献
| [1] | Dodge J S, Kulatov E, Ohta H, Uspenskii Y, Haliov S.Phys Rev B, 1999; 61:R6987 |
| [2] | Kacedon D B, Rao R A, Eom C B. Appl Phys Lett, 1997;71:1724 |
| [3] | Reich S, Tsabba Y, Cao G. J Magn Magn Mat, 1999; 202:119 |
| [4] | Yoshimuta K, Imai T, Kiyama T, Thurber K R, Hunt A W, Kosuge K. Phys Rev Lett, 1999; 83:4397 |
| [5] | Kelin L, Dodge J S, Geballe T H. Appl Phys Lett, 1995;66:2427 |
| [6] | Joy P A, Date S K, Kumar P S A. Phys Rev B, 1997; 56:2324 |
| [7] | Klein L, Kats Y, Marshall A F, Reiner J W, Geballe T H, Beasley M R, Kapitulnik A. Phys Rev Lett, 2000; 84:6090 |
| [8] | Joy P A, Kumar P S A, Date S K. J Phys Condens Matter,1998; 10:11049 |
| [9] | Williams G. In: Hein R A, Francavilla T L, Liebenberg D H eds. Magnetic Susecptibility of Superconductors and Other Spin Systems, New York: Plenum Press, 1991:475 |
| [10] | Felner I, Nowik I, Bradric I, Gospodinov. Phys Rev B,2000; 62:11332 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%