通过含MnO六元钛渣离子团结构模型及结构参数P与熔渣性质的关系,探讨了它们之间的影响规律.结果表明,随着熔渣中四配位离子的增加,其体相粘度增加,而六配位离子的作用则相反.熔渣性质与P值相关性很好,可用于熔渣性质预报.钛渣变稠是TiO2还原导致P值下降所引起的.
参考文献
| [1] | Qu Y P. Ph Dtheis, Northeastern University, Shenyang,1997(曲彦平.东北大学博士学位论文,沈阳,1997) |
| [2] | Morinaga K, Suginohara Y, Yanagase T. J Jpn Inst Met,1974; 38:658(森永健次,杉之原幸夫,柳ケ濑勉.日本金属学会志,1974;38:658) |
| [3] | Mizoguchi K, Okamoto K, Suginohara Y. J Jpn Inst Met,1982; 46:1055(溝口数一,岡本一德,杉之原幸夫.日本金属学会志,1982;46:1055) |
| [4] | Gsskell D R. Metall Trans, 1977; 5:131 |
| [5] | Kasuto Y, Nakamura T, Yanagase T. J Jpn Inst Met,1977; 41:160(楠田泰敏,中村崇,柳ケ濑勉.日本金属学会志,1977;41:160) |
| [6] | Kapoor M L, Mehrotra G M, Fronberg M G. Archive Eisenhutt, 1974; 45:663 |
| [7] | Sakawa M, Whiteway S G, Masson C R. Tetsu H agané,1976; 62:176(坂輸光弘,Whiteway S G,Masson C R.铁と钢,1976:62:176) |
| [8] | Xie D S, Mao Y W, Guo S X. Iron Steel, 1986; 21:6(谢冬生,毛裕文,郭昭信.钢铁,1986;21:6) |
| [9] | Pan J Y, Iron Steel Vanadium Titanium, 1986; 7(1): 16(潘竞业.钢铁钒钛,1986;7(1):16) |
| [10] | Cao Z. Iron Steel Vanadium Titanium, 1981; 2(5): 20(曹质.钢铁钒钛,1981;2(5):30) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%