采用DSC法研究了TiNi合金薄膜变形后的相变行为及影响机制,结果表明:变形导致TiNi薄膜马氏体发生稳定化现象,即TiNi薄膜第一次逆相变滞后,逆相变温度升高.但马氏体稳定化现象在经过一次完全相变循环后消失,且马氏体相变温度降低.变形引起TiNi合金薄膜相变行为的变化与马氏体变体储存的弹性应变能和相变不可逆能变化相关.
参考文献
| [1] | Lee A P, Ciarlo D R, Krulevitch P A, Lehew S, Trevino J, Northrup M A. Sensor Actuators, 1996; 54A: 755 |
| [2] | Makino E, Uenoyama M, Shibata T. Sensors Actuators,1998; 71A: 187 |
| [3] | Ishida A, Takei A, Miyazaki S. Thin Solid Films, 1993;228:210 |
| [4] | Luo H B, Shan F L, Huo Y L, Wang Y M. Thin Solid Films, 1999; 339:305 |
| [5] | Ishida A, Sato M, Takei A, Miyazaki S. Mater Trans JIM,1995; 36:1349 |
| [6] | Ishida A, Sato M, Takei A, Nomura K, Miyazaki S. Metall Mater Trans, 1996; 27A: 3753 |
| [7] | Luo H B, Shan F L, Huo Y L, Wang Y M. J Mater Sci Lett, 1998; 17:713 |
| [8] | Piao M, Otsuka K, Miyazaki S, Horikawa H. Mater Trans JIM, 1993; 34:919 |
| [9] | Liu Y N, Galvin S P. Acta Mater, 1997; 45:4431 |
| [10] | Liu Y N, Liu Y, Van Humbeeck J. Acta Mater, 1999; 47:199 |
| [11] | Liu Y N, Favier D. Acta Mater, 2000; 48:3489 |
| [12] | 刘晓鹏,金伟,孟长功,曹名洲,杨大智.金属学报,2001;37:589 |
| [13] | 刘晓鹏,金伟,曹名洲,杨大智,陈非霞.金属学报,待发表 |
| [14] | Liu Y, Xie Z, Van Humbeeck J, Delaey L. Scr Mater, 1999;41:1273 |
| [15] | Xie Z, Liu Y, Van Humbeeck J. Acta Mater, 1998; 46:1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%