导出了多相合金组成相结构体积分数以及用成分的原子分数与质量分数求得的相含量之间的关系.结果表明,组成相结构体积分数是由质量分数算得的相含量和相密度的函数,尽管用原子分数与用质量分数求得的合金相含量以及与该相的结构体积分数可能在数值上相差甚小,但它们数值来源的物理量不同,其间有定量关系,并可在一定条件下反映出其各自的特征.
参考文献
| [1] | Nathal M V, Ebert L J. Metall Trans, 1985; 16A: 1849 |
| [2] | Glatzel U, Feller-Kniepmeier M. Scr Metall Mater, 1991;25:1845 |
| [3] | Melow T, Zhu J W, Wahi R P. Z Metallkd, 1994; 85:9 |
| [4] | Lempke H, Wang Y, Mukherji D, Chen W, Wiedenmann A, Wahi R P. Z Metallkd, 1994; 87:286 |
| [5] | Schulze C, Feller-Kniepmeier M. Scr Mater, 2001; 44:731 |
| [6] | Glatzel U. Microstructure and Internal Strains of Undeformed and Creep Deformed Samples of a Nickel-base Superalloy. Berlin: Verlag Dr Koster, 1994:10 |
| [7] | Schmidt R, Feller-Kniepmeier. Metall Trans, 1992; 23A: 745 |
| [8] | Schmidt R, Feller-Kniepmeier. Scr Metall Mater, 1992;26:1919 |
| [9] | Harada H, Yamazaki M, Koizumi Y, Sakuma N, Furuya N, Kamiya H. High Temperature Alloys for Gas Turbines 1982, Liege, Belgium: D.Reidel Publishing Co., 1982; 721 |
| [10] | Volkl R, Glatzel U, Feller-Kniepmeier. Scr Mater, 1998;38:893 |
| [11] | Peng Z F, Yan P, Luo Y S, Ren Y Y, Zhao J C. Acta Metall Sin, to be published(彭志方,燕平,骆宇时,任遥遥,赵京晨.金属学报,待发表) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%