研究了原始晶粒尺寸为270 μm的Ni-45Al单相合金的高温变形行为.结果表明,该合金在1000-1100℃温区,1×10-4-2.5×10-2s-1的应变速率范围内呈现超塑性变形;在1075℃应变速率为2.5×10-4s-1时,最大延伸率可达245%,相应的应变速率敏感指数为0.3,表观激活能为320 KJ/m01.在超塑性变形过程中发生发生连续回复和再结晶,导致原始大晶粒组织经超塑性变形后的显著细化.
参考文献
| [1] | Lin D L, Shan A D, Li D Q. Scr Metall Mater, 1994; 31:1455 |
| [2] | Li D Q, Shan A D, Liu Y, Li D L. Scr Metall Mater, 1995;33:681 |
| [3] | Lin D L, Shan A D, Chen M W. Intermetallics, 1996; 4:489 |
| [4] | Liu Y, Li D Q, Lin D L. Scr Metall Mater, 1996; 34:1095 |
| [5] | Lin D L, Liu Y. Mater Sci Eng, 1999; A268:83 |
| [6] | Gu Y F, Lin D L, Shan A D, Liu Y, Liu Z Y. Acta Metall Sin, 1997; 33:325(谷月峰,林栋梁,单爱党,刘毅,刘震云.金属学报,1997;33: 325) |
| [7] | Liu Z Y, Lin D L,Gu Y F, Cao P,Lie C M, Huang B Y.Acta Metall Sin, 1996; 32:1139(刘震云,林栋梁,谷月峰,曹鹏,雷长明,黄伯云.金属学报,1996;33:1139) |
| [8] | Sun F, Lin D L. Scr Mater, 2001; 44:665 |
| [9] | Du X H, Guo J T, Zhou B D. Scr Mater, 2001; 45:69 |
| [10] | Jiang D M, Lin D L. Mater Sci Lett, in press |
| [11] | Kim W Y, Hanada S, Sakai T. Mater Sci Eng, 1998; A248:78 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%