对M963合金熔体进行了过热处理并在1248 K/225 MPa条件下测试了其持久性能.结果表明:随熔体过热温度的升高,铸态组织中的初生MC碳化物不断细化和均匀分布,合金的持久断裂寿命和塑性明显提高;但温度高达2023 K的熔体过热处理,使合金中的气体含量升高,导致显微疏松增加,持久性能降低.在1923 K温度下进行熔体过热处理,可使M963合金在1248 K/225 MPa条件下的持久寿命和持久塑性同时提高一倍以上.
参考文献
| [1] | Sims C T, Stoloff N S, Hagel W C. Superalloy Ⅱ. New York: John Wiley & Sons, Inc., 1987:63 |
| [2] | Cheng G L. Superalloy. Beijing: Metallurgy Industy Press, 1985:167(陈国良.高温合金学.北京:冶金工业出版社.1988:167) |
| [3] | Zheng Y R. Acta Metall Sin, 1999; 35:1242(郑运荣.金属学报,1999;35:1242) |
| [4] | Burton C J. Proceedings of the Third International Symposium on Superalloys. Baton Rouge: Claitor Publishing,1976:147 |
| [5] | Novak L, Potocky L, Lovas A, Kisdi-Koszo E, Takacs J. J Magn Mater, 1980; 19:149 |
| [6] | Takayama S, Oi T. J Appl Phys, 1997; 50:1595 |
| [7] | Bian X F, Wang W M. Mater Lett, 2000; 44:54 |
| [8] | Bian X F, Li H, Zhang L, Ma J J, Max T. Chin Sci Bulletin, 1996; 41:873 |
| [9] | Yuan C, Sun X F, Yin F S, Guan H R, Hu Z Q, Zheng Q,Yu Y. J Mater Sci Technol, 2001; 17:425 |
| [10] | Yin F S, Yuan C, Sun X F, Guan H R, Hu Z Q. Heat Treat Met, 2001; 26(7): 1(殷凤仕,袁超,孙晓峰,管恒荣,胡壮麒.金属热处理,2001; 26 (7): 1) |
| [11] | Yin F S Sun X F, Yuan C, Guan H R, Hu Z Q. Trans Nonferrous Met Soc Chin, 2002; 12:83 |
| [12] | Yin F S, Sun X F, Yuan C, Guan H R, Hu Z Q. J Wuhan Univ Technol, 2002; 17:42 |
| [13] | Liu L, Zhen B L, Banerji A, Reif W, Sommer F. Scr Met,1994; 30:593 |
| [14] | Burton C J, Boesch W J. Met Prog, 1975; 10:121 |
| [15] | Liu L, Sommer F, Fu H Z. Scr Metall, 1994; 30:587 |
| [16] | Fernandez R, Lecomte J C, Kattamis T Z. Metall Trans,1978; 9A: 1381 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%