为了降低激光熔敷Fe-B涂层的高度脆性,使用不同成分的B4C和Fe-Ti合金混合粉末在奥氏体不锈钢基体上进行了激光熔敷,得到了具有TiB2晶须强化的复合Fe-Ti-B涂层.该涂层在保持原来Fe-B涂层的高硬度的同时,其抗裂性能亦得到了改善.
参考文献
| [1] | Draper C W, Poate J M. Int Met Rev, 1985; 30:85 |
| [2] | Mollart T P, Baker M, Haupt J, Steiner A, Hammer P,Gissler W. Surf Coat Technol, 1995; 74-75:491 |
| [3] | Yu Zuo, Latanision R M. J Mater Sci, 1992; 27:3014 |
| [4] | Wang X B, Liu H. Surf Coat Technol, 1998; 106:156 |
| [5] | Molian P, Rajasekhara H. Wear, 1987; 14:19 |
| [6] | Pei Y T, Ouyang J H, Lei T C. Surf Coat Technol, 1996;81:131 |
| [7] | Pei Y T, Ouyang J H, Lei T C. Metall Mater Trans, 1996;A27:391 |
| [8] | Zhang S Y, Wang B B, Zheng K Q. Acta Phys Sin, 1994;43:678(张思玉,王必本,郑克全.物理学报,1994;43:678) |
| [9] | Ariely S, Shen J, Bamberger M, Dausiger F, Hugel H. Surf Coat Technol, 1991; 45:403 |
| [10] | Abbas G, West D R F. Wear, 1991; 43:353 |
| [11] | Elders J, Quist P A, Rooswijk B, Van Voorst J D W, Van Nieuwkoop J. Surf Coat Technol, 1991; 45:105 |
| [12] | Dey G K, Arya A, Sekhar J A. J Mater Res, 2000; 15:63 |
| [13] | Chang Hee Lee, Euipak Yoon. Surf Coat Technol, 1998;99:203 |
| [14] | Samsonov G V. Handbook of Refractory Compounds.Moskva: 1963:307(СамсоновГВ. ТугодлавкиеСоединнияМеталлургиздат. Москва: 1963: 307) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%