通过研究Nd4.5Fe76.5-xGaxCo1.0B18(x=0-0.6,(原子分数,%))纳米复合粘结磁体的微结构和矫顽力,发现Ga在晶界富Nd相中的分布高于(Fe,Co)3B和Nd2(Fe,Co)14B相,矫顽力随Ga含量的增加是先下降然后增加,当Ga含量较低时(x=0.2),磁体的矫顽力随退火时间的变化关系出现一个明显的峰值,这些现象可用合金的微结构和纳米双相复合磁体的交换耦合作用来解释.
参考文献
| [1] | Skomski R, Coey J M D. Phys Rev, 1993; 48B: 15812 |
| [2] | Fischer R, Schrefl T, Kronmiiller H, Fidler J. J Magn Magn Mater, 1996; 153:35 |
| [3] | Schrefl T, Fidler J, Kronmüller H. Phys Rev, 1994; 49B:6100 |
| [4] | Kronmüller H, Fischer R, Seeger M, Zern A. J Phys D:Appl Phys, 1996; 29:2274 |
| [5] | Fischer R, Schrefl T, Kronmüller H, Fidler J. J Magn Magn Mater, 1995; 150:329 |
| [6] | Sinnecker E H C P, Ferrara E, Tiberto P. J Magn Magn Mater, 1999; 196-197:291 |
| [7] | Gried B, Fritz k. J Appl Phys, 1991; 70:6447 |
| [8] | Ping D H, Hono K, Hirosawa S. J Appl Phys, 1998; 83:7769 |
| [9] | Zhu M G, Dong S Z, Li X M, Li W. Met Fanct Mater,2001; 8:26(朱明刚,董生智,李岫梅,李卫.金属功能材料,2001;8:26 |
| [10] | Chu Y L, Xiong L Y, Sun X K. Acta Metall Sin, 1998; 34423(初业隆,熊良钺,孙校开.金属学报,1998;34:423) |
| [11] | Panagiotopoulos I, Withanawasam L, Hadjipanayis G J.J Magn Magn Mater, 1996; 152:353 |
| [12] | Gao R W, Dai Y Y, Li W. Progr Phys. 2001; 21:131(高汝伟,代由勇,李卫.物理学进展,2001;21:131) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%