采用表面机械研磨处理(SMAT)在AISI 304不锈钢上制备出纳米结构表层,研究纳米化行为及其对硬度的影响.结果表明:经过SMAT后,样品表面形成了厚度约为30μm的纳米晶层,显微组织由平均晶粒尺寸约为10 nm的单一马氏体相演变为尺寸稍大的双相组织;在距表面30-300 μm的范围内,显微组织由以亚微米级的奥氏体多系孪晶为主逐渐演变为单系孪晶.表面纳米化是晶粒碎化与纳米尺度新相形成共同作用的结果.与心部相比,表面硬度显著提高.
参考文献
| [1] | Valiev R Z, Krasilnikov A V, Tsenev N K. Mater Sci Eng,1991; A137:35 |
| [2] | Vailev R Z, Ivanisenko Y V, Rauch E F, Baudelet B. Acta Mater, 1996; 44:4705 |
| [3] | Imayev R M, Imayev V M, Salishohev G A. J Mater Sci,1992; 27:4465 |
| [4] | Saito Y, Tsuji N, Utsunomiya H, Sakai T, Hong R G. Scr Mater, 1998; 39:1221 |
| [5] | Lu J. Proc 4th Inter Conf on Residual Stresses, Baltimore:Soc Exp Mechanics, 1994:1154 |
| [6] | Lu K, Lu J. Chinese Patent(99122670.4), 1999.(卢柯,吕坚,中国发明专利(99122670.4),1999) |
| [7] | Lu K, Lu J. J Mater Sci Technol, 1999; 15:193 |
| [8] | Liu G, Wang S C, Lou X F, Lu J, Lu K. Scr Mater, 2001;44:1791 |
| [9] | Tao N R, Sui M L, Lu K, Lu J. Nanostruc Mater, 1999;11:443 |
| [10] | Liu G, Lu J, Lu K. Mater Sci Eng, 2000; A286:91 |
| [11] | Yong X P, Liu G, Lu J, Lu K. Acta Metall Sin, 2002; 38:157(雍兴平,刘刚,吕坚,卢柯.金属学报,2002;38:157) |
| [12] | Liu G,Yong X P,Lu J,Lu K.Chin Surf Eng,2001;52:1(刘刚,雍兴平,吕坚,卢柯.中国表面工程,2001;52:1) |
| [13] | Klug H P, Alexander L E. X-Ray Diffraction Procedures For Polycrystalline and Amorphous Materials, New York:Wiley, 1974:661 |
| [14] | Olson G B, Cohen M. Metall Trans, 1975; A6:791 |
| [15] | Yong X P, Liu G, Lu J, Lu K. J Mater Sci Technol, 2003;19 (to be printed) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%