对亚包晶、过包晶以及接近包晶点成分的Zn-Cu二元合金进行了定向凝固实验,研究其在45 K/mm的温度梯度以及2-6400μm/s凝固速度下的组织选择及演化规律,发现Zn-2%Cu的低速凝固组织为η相单相生长,高速下为η相胞晶+胞晶间ε相的组织;Zn-2.7%Cu,Zn-3%Cu以及Zn-4%Cu的低速凝固组织为η相基体+ε相定向枝晶,高速凝固组织为η相胞晶+ε相等轴晶.基于最高界面生长温度判据,在充分形核假设下对凝固过程中的相选择规律进行了分析,并与实验结果较好的吻合.
参考文献
| [1] | Kerr H W, Kurz W. Int Mater Rev, 1996; 4:41 |
| [2] | Boettinger W J, Coriell S R, Greer A L, Karma A, Kurz W, Rappaz M, Trivedi R. Acta Mater, 2000; 48:43 |
| [3] | Caroli B, Caroli C, Roulet B. Acta Metall, 34, 1986; 34:1867 |
| [4] | Hillert M. Solidification and Casting of Metals. London:The Metals Society, 1979:242 |
| [5] | Umeda T, Okane T, Kurz W. Acta Mater, 1996; 44:4209 |
| [6] | Vandyoussefi M, Kerr H W, Kurz W. In: Beech J, Jones H eds., Proc 4th Int Conf on Solidification Processing.Sheffield: The University of Sheffield, 1997:564 |
| [7] | Wang M, Lin X, Su Y P, Shen S J, Huang W D. Acta Metall Sin, 2002; 38:337(王猛,林鑫,苏云鹏,沈淑娟,黄卫东,金属学报,2002;38:337) |
| [8] | Huang W D, Lin X, Wang M, Shen S J, Su Y P, Liu Z X.Sci Chin, 2002; 45E: 458 |
| [9] | Aziz M J, Kaplan T. Acta Metall, 1988; 36:2335 |